Post consumer pet depolymerization by acid hydrolysis

The reaction of post-consumer poly(ethylene terephthalate) with aqueous solutions of sulfuric acid 7.5M was investigated in terms of temperature, time and particle size. The reaction extent reached 80% in four days at 100 degrees C and 90% in 5 hours at 135 degrees C. TPA obtained was purified and considered in the same level of quality of the commercial one after tests of elemental analysis, particle size and color. It was concluded that the hydrolysis occurred preferentially at the chain ends and superficially, having as controller mechanism the acid diffusion into the polymer structure. The shrinking-core model can explain the reaction kinetics.

Additional steps in mechanical recyling of PET

This study presents the laboratory scale results of an extra step in Poly (ethylene terephthalate) - PET mechanical recycling (grinding, washing, drying and reprocessing): a chemical washing after the conventional one. Cooking oil PET bottle flakes were washed in water and then subjected to a reaction with an aqueous solution of sodium hydroxide 5 M at 90 degrees C for 10 min (chemical washing). After rinsing and drying, the flakes were characterized by thermogravimetry, gas chromatography and elemental analysis tests. The results indicated that the chemically washed material had higher purity than PET washed only with water: 99.3% and 96.7%, respectively, which undoubtedly implies properties, applications and prices closer to those of virgin resin. The production of purified terephthalic acid (TPA) from the chemical washing residue was optimized and reached a purity of 99.6%. Despite the results, the use of chemically washed PET and of TPA obtained is not recommended for direct contact with food, since they still contain some impurities. (C) 2009 Elsevier Ltd. All rights reserved.

Characterization of Post-Consumer PET after Removal of the Original Surface: Influence of Raw Material

Post-consumer cooking oil and soft drink PET bottles (PEToil and PETsoft drink) were ground and washed only with water (conventional washing). The polymer was then chemically washed (10min in an aqueous solution of sodium hydroxide 5mol center dot L-1 at 90 degrees C) and rinsed. The materials before and after chemical washing were characterized by intrinsic viscosity, differential scanning calorimetry, thermogravimetry, elemental analysis, scanning electron microscopy with X-ray spectrum microanalysis, and gas chromatography coupled to mass spectrometry. The results indicated that conventionally washed PEToil is the material that most differs among the four tested ones, and that the other three are more similar to each other and to what is expected for pure PET. For example, the composition of PEToil washed only in water contained 30 volatile organic compounds, 5 nonvolatile compounds, and 7 metals, while PETsoft drink washed conventionally and chemically contained 5 volatile organic compounds and no metal or nonvolatile organic compounds.