Effect of oxygen on the electrical characteristics of field effect transistors formed from electrochemically deposited films of poly(3-methylthiophene)

Field effect devices have been formed in which the active layer is a thin film of poly(3-methylthiophene) grown electrochemically onto preformed source and drain electrodes. Although a field effect is present after electrochemical undoping, stable device characteristics with a high modulation ratio are obtained only after vacuum annealing at an elevated temperature, and only then if the devices are held in vacuo. The polymer is shown to be p type and the devices operate in accumulation only. The hole mobility in devices thermally annealed under vacuum is around 10 -3 cm 2 V -1 s -1. On exposure to ambient laboratory air, the device conductance increases by several orders of magnitude. This increase may be reversed by subjecting the device to a further high-temperature anneal under vacuum. Subsidiary experiments show that these effects are caused by the reversible doping of the polymer by gaseous oxygen.

Electrical study of impurity states in conjugated polymers

Schottky diodes resulting from an intimate contact of aluminum on electro-deposited poly(3-methylthiopene), PMeT, have been studied by admittance spectroscopy, capacitance-voltage and current-voltage measurements, and optically-induced current transients. The loss-tangents show the existence of interface states that can be removed by vacuum annealing, also visible in the transients. Furthermore, the CV curves don't substantiate the idea of movement of the dopant ions.

Electrical characterization of semiconducting polymers

Schottky diodes resulting from an intimate contact of aluminum on electrodeposited poly(3-methylthiopene) were studied by admittance spectroscopy, capacitance-voltage measurements and voltaic and optically-induced current and capacitance transients. The loss tangents show the existence of interface states that can be removed by vacuum annealing. Furthermore, the C-V curves contradict the idea of movement of the dopant ions.

Schottky barrier diodes from semiconducting polymers

Schottky barrier diodes based on Al/poly(3-methylthiophene)/Au have been fabricated and their electrical behaviour investigated. I-V characteristics revealed a dependence on the fabrication conditions, specifically on the time under vacuum prior to evaporation of the rectifying contact and post-metal annealing at elevated temperature. The available evidence is consistent with the formation of a thin insulating layer between the metal and the polymer following these procedures. Long periods under vacuum prior to deposition of the aluminium electrode reduced the likelihood of such a layer forming. Capacitance-voltage plots of the devices were stable to voltage cycling, so long as the forward voltage did not exceed similar to 1 V. Above this a small degree of hysteresis was observed, which is attributed to the filling/emptying of interface states or traps in the polymer.