Bias-induced threshold voltages shifts in thin-film organic transistors

An investigation into the stability of metal-insulator-semiconductor (MIS) transistors based on alpha-sexithiophene is reported. In particular, the kinetics of the threshold voltage shift upon application of a gate bias has been determined. The kinetics follow stretched-hyperbola-type behavior, in agreement with the formalism developed to explain metastability in amorphous-silicon thin-film transistors. Using this model, quantification of device stability is possible. Temperature-dependent measurements show that there are two processes involved in the threshold voltage shift, one occurring at Tapproximate to220 K and the other at Tapproximate to300 K. The latter process is found to be sample dependent. This suggests a relation between device stability and processing parameters. (C) 2004 American Institute of Physics.

Electrical characterization of the rectifying contact between aluminium and electrodeposited poly(3-methylthiophene)

A detailed investigation both of the DC and of the AC electrical properties of the Schottky barrier formed between aluminium and electrodeposited poly(3-methylthiophene) is reported. The devices show rectification ratios up to 2 x 10(4) which can be increased further after post-metal annealing. The reverse characteristics of the devices follow predictions based on the image-force lowering of the Schottky barrier, from which the doping density can be estimated, As the forward voltage increases, the device current is limited by the bulk resistance of the polymer with some evidence for injection limitation at the gold counter-electrode at high bias. In the bulk-limited regime, the device current is thermally activated near room temperature with an activation energy in the range 0.2-0.3 eV. Below about 150 K the device current is almost independent of temperature. Capacitance-voltage plots obtained at frequencies well below the device relaxation frequency indicate the presence of two distinct acceptor states, A set of shallow acceptor states are active in forward bias and are believed to determine the bulk conductivity of the polymer. A set of deeper accepters are active only for very small forward voltages and for all reverse voltages, namely when band banding causes the Fermi energy to cross these states. The density of these deeper states is approximately an order of magnitude greater than that of the shallow states. Evidence is presented also for the influence of fabrication conditions on the formation of an insulating interfacial layer at the rectifying interface. The presence of such a layer leads to inversion at the polymer surface and a modification of the I-V characteristics.

Charge transport in poly(3-methylthiophene) schottky barrier diodes

Schottky-barrier devices were formed from electropolymerised films of poly (3-methylthiophene) (PMeT). Thermal annealing of a partially undoped film led to diodes with rectification ratios as high as 5900 at 1 V and 50,000 at 2.5 V and ideality factors slightly above 2. The temperature dependence of ac loss tangent and forward currents are identical suggesting that bulk effects dominate device behaviour event at very low forward voltages. Below 250 K forward currents are essentially independent of temperature. Preliminary TSC measurements show the presence of at least two trapping levels in the devices. © 1993.