Electronic transport in field-effect transistors of sexithiophene

The electronic conduction of thin-film field-effect-transistors (FETs) of sexithiophene was studied. In most cases the transfer curves deviate from standard FET theory; they are not linear, but follow a power law instead. These results are compared to conduction models of "variable-range hopping" and "multi-trap-and-release". The accompanying IV curves follow a Poole-Frenkel (exponential) dependence on the drain voltage. The results are explained assuming a huge density of traps. Below 200 K, the activation energy for conduction was found to be ca. 0.17 eV. The activation energies of the mobility follow the Meyer-Neldel rule. A sharp transition is seen in the behavior of the devices at around 200 K. The difference in behavior of a micro-FET and a submicron FET is shown. (C) 2004 American Institute of Physics.

Electronic levels in MEH-PPV

pn-Junctions of MEH-PPV on top of heavily doped n-type silicon were used in electrical measurements. Through deep-level transient-spectroscopy (DLTS)-like measurements, four traps (two majority and two minority traps) could be identified on top of the shallow acceptor level responsible for conduction. Furthermore, evidence is found for interface states. (C) 2000 Published by Elsevier Science S.A. All rights reserved.

Charge transport in poly(3-methylthiophene) schottky barrier diodes

Schottky-barrier devices were formed from electropolymerised films of poly (3-methylthiophene) (PMeT). Thermal annealing of a partially undoped film led to diodes with rectification ratios as high as 5900 at 1 V and 50,000 at 2.5 V and ideality factors slightly above 2. The temperature dependence of ac loss tangent and forward currents are identical suggesting that bulk effects dominate device behaviour event at very low forward voltages. Below 250 K forward currents are essentially independent of temperature. Preliminary TSC measurements show the presence of at least two trapping levels in the devices. © 1993.