Ultrasonic wave reflection measurements on self-compacting pastes and concretes

The objective of this study was to extend the use of combined longitudinal (P-wave) and shear (S-wave) ultrasonic wave reflection (UWR) to monitor the setting and stiffening of self-compacting pastes and concretes. An additional objective was to interpret the UWR responses of various modified cement pastes. A polymeric buffer with acoustic impedance close to that of cement paste, high impact polystyrene, was chosen to obtain sensitive results from the early hydration period. Criteria for initial and final set developed by our group in a prior study were used to compute setting times by UWR. UWR results were compared with standard penetration measurements. Stiffening behavior and setting times for normal cement pastes, pastes modified with mineral and chemical admixtures, self-compacting pastes, and concretes were explored using penetration resistance, S-wave and P-wave reflection. All three methods showed that set times of pastes varied linearly with w/c, that superplasticizer and fly ash delayed the set times of pastes, and that differences in w/cm, sp/cm, and fa/cm could be detected. Final set times determined from UWR correlated well with those from penetration resistance. Initial set times from S-wave reflection did not correlate very well with those from penetration resistance. Final set times from P-wave and S-wave reflection were roughly the same. Pastes with different chemical admixtures were tested, and the effects of these admixtures on stiffening were determined using UWR. Self-compacting concretes were studied using UWR, and their response and setting times were largely similar to that of corresponding self-compacting pastes. The P-wave reflection response was explored in detail, and the phenomenon of partial debonding and the factors affecting it were explained. Partial debonding is probably caused by autogenous shrinkage at final set, and was controlled and limited by water. The extent of partial debonding was higher with the transducers placed on the side as opposed to the bottom, and the S-wave transducer seemed to promote debonding in the P-wave reflection, whereas the P-wave transducer seemed to reduce debonding in the S-wave reflection. Simultaneous formwork pressure testing and UWR were performed; however, no clear correlation was seen between the two properties.