The effect of cationic-anionic polyelectrolyte multilayer surface treatment on inkjet ink spreading and print quality

The focus of the work reported in this thesis was to study and to clarify the effect of polyelectrolyte multilayer surface treatment on inkjet ink spreading, absorption and print quality. Surface sizing with a size press, film press with a pilot scale coater, and spray coating, have been used to surface treat uncoated wood-free, experimental wood-free and pigmentcoated substrates. The role of the deposited cationic (polydiallydimethylammonium chloride, PDADMAC) and anionic (sodium carboxymethyl cellulose, NaCMC) polyelectrolyte layers with and without nanosilica, on liquid absorption and spreading was studied in terms of their interaction with water-based pigmented and dye-based inkjet inks. Contact angle measurements were made in attempt to explain the ink spreading and wetting behavior on the substrate. First, it was noticed that multilayer surface treatment decreased the contact angle of water, giving a hydrophilic character to the surface. The results showed that the number of cationic-anionic polyelectrolyte layers or the order of deposition of the polyelectrolytes had a significant effect on the print quality. This was seen for example as a higher print density on layers with a cationic polyelectrolyte in the outermost layer. The number of layers had an influence on the print quality; the print density increased with increasing number of layers, although the increase was strongly dependent on ink formulation and chemistry. The use of nanosilica clearly affected the rate of absorption of polar liquids, which also was seen as a higher density of the black dye-based print. Slightly unexpected, the use of nanosilica increased the tendency for lateral spreading of both the pigmented and dye-based inks. It was shown that the wetting behavior and wicking of the inks on the polyelectrolyte coatings was strongly affected by the hydrophobicity of the substrate, as well as by the composition or structure of the polyelectrolyte layers. Coating only with a cationic polyelectrolyte was not sufficient to improve dye fixation, but it was demonstrated that a cationic-anionic-complex structure led to good water fastness. A threelayered structure gave the same water fastness values as a five-layered structure. Interestingly, the water fastness values were strongly dependent not only on the formed cation-anion polyelectrolyte complexes but also on the tendency of the coating to dissolve during immersion in water. Results showed that by optimizing the chemistry of the layers, the ink-substrate interaction can be optimized.