PREPARATION, STRUCTURE AND INFLUENCE OF VALENCE STATE ON LASR2-XCAXV3O9+/-Y

New compounds LaSr2-xCa-(x)V3O9+/-y (x = 0.0, 0.67, 1.0, 1.33 and 2.0) have been synthesized with a simple new method X ray powder diffraction results indicate that they are single compound. Their lattice constants are calculated. The structure of LaSr2-xCa(x)V39+/-y changed from cubic to orthorhombic and back to cubic with the increase of calcium content. The results of weight gain in TG and XPS curves show that vanadium with lower valent state is oxidized to higher valent state at higher temperature. The oxygen content of new compounds are calculated from the weight gain. It is shown that V3+ and V4+ may coexist in LaSr2-xCa(x)V3O9+/-y. These compounds show that low resistivity.