Nanocrystalline La2Mo2O9 and its characterization
Data(s) |
2004
|
---|---|
Resumo |
In this work, both the thermal expansion and electrical conductivity of nanocrystalline La2Mo2O9 were studied. The nanocrystalline powder of La2Mo2O9 was obtained by sol-gel method, and with the help of SHP (superhigh pressure) up to 4.5 x 10(4) atm at 700 degrees C for a short time, and the nanocrystalline powder was densified without obvious particle size growth. The electrical conductivity of nanocrystalline La2Mo2O9 was one order of magnitude lower than that of the microcrystalline sample at the same temperature. Owing to the phase transition, the microcrystalline La2MO2O9 has an abrupt increase of thermal expansion with a peak value of 48 x 10(-6) K-1 at 556 degrees C. For the nanocrystalline material, the peak value increases to 112 x 10(-6) K-1 at 520 degrees C. On the other hand, above 600 degrees C the significant growth of particle size of the nanocrystalline La2Mo2O9 was observed, accompanying by a tremendous increase of thermal expansion with a peak value of 1565 x 10(-6) K-1 at 620 degrees C. The electrical conductivity of La1.6Nd0.4Mo2O9 at 800 degrees C is 0.14 S center dot cm(-1) which is about one third higher than that of La2Mo2O9. |
Identificador | |
Idioma(s) |
英语 |
Fonte |
Li Q;Xia T;Li JY;Liu XD;Ma XF;Meng J;Cao XQ.Nanocrystalline La2Mo2O9 and its characterization,JOURNAL OF RARE EARTHS,2004,22():102-106 |
Palavras-Chave | #OXIDE-ION CONDUCTORS #ELECTRICAL-CONDUCTIVITY |
Tipo |
期刊论文 |