Estudo do crescimento bacteriano e da aplicação de procedimentos de limpeza e desinfecção no aço inoxidável 304L
Contribuinte(s) |
Márcia Monteiro Machado Gonçalves Marta Antunes Pereira Langone Lilian Ferreira de Senna Dalva Cristina Baptista do Lago Eliana Flávia Camporese Sérvulo |
---|---|
Data(s) |
27/04/2012
|
Resumo |
Técnicas de limpeza química ou mecânica são comumente empregadas para evitar a formação de biofilmes e problemas associados com a colonização de superfícies por micro-organismos. Neste trabalho, amostras de aço inox 304L foram submetidas a ensaios acelerados de crescimento de biofilme, o qual foi posteriormente removido por tratamentos de limpeza e desinfecção (choque térmico com água a 70C por 1h, limpeza com ácido fosfórico 20 % v/v por 30min e desinfecção com peróxido de hidrogênio 0,17 % v/v por 1h). Com o objetivo de verificar a influência destes tratamentos na remoção do biofilme, este foi caracterizado (por quantificação microbiana e análises de espectroscopia de impedância eletroquímica - EIE), antes e após a aplicação dos tratamentos. Dois casos foram estudados. No primeiro caso, simularam-se condições presentes em tubulações de ambientes hospitalares e sistemas de distribuição de água quente. O micro-organismo utilizado foi a bactéria Serratia marcences. O processo de formação de biofilme e posterior limpeza e desinfecção foi realizado de modo contínuo durante 15 semanas. Os resultados de quantificação microbiana e de EIE mostraram que desde a primeira semana de exposição e ao longo dos ensaios, formou-se um biofilme aderente à superfície do aço e que o emprego dos tratamentos de limpeza e desinfecção não foi eficaz na remoção do biofilme. Em um segundo caso, simularam-se condições presentes em tubulações da indústria de água mineral, empregando-se a bactéria Pseudomonas aeruginosa. Neste caso, as técnicas de limpeza e desinfecção foram aplicadas individualmente e em conjunto. A aplicação de choque térmico, assim como da limpeza ácida, sobre um biofilme com 72 h de formação foi capaz de eliminar as bactérias viáveis, presentes na superfície do aço. Entretanto, a desinfecção com peróxido de hidrogênio não foi capaz de eliminá-las. Nas duas condições, porém, as análises de EIE do sistema aço/biofilme mostraram que o mesmo não foi completamente removido da superfície do metal. Correlacionando os dois casos, pode-se inferir que a superfície do aço inox 304L é rapidamente colonizada pelas duas espécies microbianas e que as técnicas de limpeza e desinfecção são capazes de reduzir e até eliminar as células viáveis, embora não removam completamente o biofilme da superfície. Por outro lado, é importante ressaltar que fatores como a arquitetura, espessura e porosidade do biofilme, e propriedades intrínsecas da superfície, são fatores que afetam os valores de impedância medidos, sendo necessário considerá-los na análise, tanto da formação do biofilme, quanto dos efeitos dos procedimentos de limpeza e desinfecção Techniques for chemical or mechanical cleaning are usually employed to prevent the formation of biofilm and the problems associated with the colonization of surfaces by micro-organisms. In this work, samples of 304 L stainless steel were submitted to experiments of accelerated growth of biofilm, which was subsequently removed by cleaning and disinfection treatment (heat shock with water at 70 C for 1h, cleaning with phosphoric acid 20% v/v for 30 min and disinfection with hydrogen peroxide 0,17% v/v for 1h). In order to verify the influence of these treatments on biofilm removal, analyses of microbial quantification and electrochemical impedance spectroscopy (EIS), before and after the treatments were employed. Two cases were studied. In the first case, it was simulated the conditions found in piping for hospital environment and systems for the distribution of hot water. The micro-organism used was the bacteria Serratia marcences. The process of biofilm formation and subsequent cleaning and disinfection was performed continuously for 15 weeks. The results of measurement of microbial and EIS showed that since the first week of exposure and during the testing, an adherent biofilm was formed on the steel surface and that the use of cleaning and disinfecting treatments were not effective in removing biofilm. In a second case, it was simulated the conditions present in the pipes of the mineral water industry, using the bacterium Pseudomonas aeruginosa. In this case, the cleaning and disinfection techniques were applied individually and as a whole. The application of heat shock, as well as acid cleaning, to the biofilm formated after 72 h was able to eliminate the viable bacteria present in the steel surface. However, disinfection with hydrogen peroxide was not able to eliminate them. In both conditions, however, the EIS analysis of the steel/biofilm system showed that it was not satisfactorily removed from the metal surface. Comparing the two cases, it can be inferred that the surface of 304L stainless steel is rapidly colonized by the two microbial species studied and that the cleaning and disinfection techniques are able to reduce and even eliminate viable cells, although they could not completely remove the biofilm from the surface. On the other hand, it is important to note that factors such as properties of the electrode surface (roughness, porosity and adsorption), the electrode potential, and the architecture, thickness and porosity of the biofilm, are factors that affect the measured impedance values, it is necessary to consider them in the analysis of biofilm formation and effects of cleaning and disinfection |
Formato |
|
Identificador |
http://www.bdtd.uerj.br/tde_busca/arquivo.php?codArquivo=7315 |
Idioma(s) |
pt |
Publicador |
Biblioteca Digital de Teses e Dissertações da UERJ |
Direitos |
Liberar o conteúdo dos arquivos para acesso público |
Palavras-Chave | #Biofilme #aço inox 304L #tratamentos de limpeza e desinfecção #espectroscopia de impedância eletroquímica #Biofilm #stainless steel 304L #cleaning and disinfection treatments #electrochemical impedance spectroscopy #TECNOLOGIA QUIMICA |
Tipo |
Eletronic Thesis or Dissertation Tese ou Dissertação Eletrônica |