Transparent Ni2+-doped MgO-Al2O3-SiO2 glass ceramics with broadband infrared luminescence
Data(s) |
2006
|
---|---|
Resumo |
We report on transparent Ni2+-doped MgO-Al2O3-SiO2 glass ceramics with broadband infrared luminescence. Ni2+-doped MgO-Al2O3-SiO2 glass is Prepared by using the conventional method. After heat treatment at high temperature, MgAl2O4 crystallites are precipitated, and their average size is about 4.3nm. No luminescence is detected in the as-prepared glass sample, while broadband infrared luminescence centred at around 1315nm with full width at half maximum (FWHM) of about 300nm is observed from the glass ceramics. The observed infrared emission could be attributed to the T-3(2g)(F-3) -> (3)A(2g)(F-3) transition of octahedral Ni2+ ions in the MgAl2O4 crystallites of the transparent glass ceramics. The product of the fluorescence lifetime and the stimulated emission cross section is about 1.6 X 10(-24) s cm(2). |
Identificador | |
Idioma(s) |
英语 |
Fonte |
吴伯涛;周时凤;邱建荣;Peng Xing-Ying;Yang Lu-Yun;Jiang Xiong-Wei;Zhu Cong-Shan.,Chin. Phys. Lett.,2006,23(10):2778-2781 |
Palavras-Chave | #OPTICAL-PROPERTIES #UP-CONVERSION #SPECTROSCOPY #NANOCRYSTALS #ABSORPTION #OPERATION #SYSTEM #IONS #YB3+ |
Tipo |
期刊论文 |