Pyroelectric and second harmonic responses from LiTaO3 nanocrystallites evolved in a Li2O-B2O3-Ta2O5 glass system

Dendritic growth of trigonal and square bipyramidal structures of LiTaO3 nanocrystallites, of 19-30 nm size, was observed when 1.5Li(2)O-2B(2)O(3)-0.5Ta(2)O(5) glasses were subjected to controlled heat treatment between 530 degrees C and 560 degrees C/3 h. X-ray diffraction and Raman spectral studies carried out on the heat-treated samples confirmed the formation of a LiTaO3 phase along with a minor phase of ferroelectric Li2B4O7. The sample that was heat-treated at 550 degrees C/3 h was found to possess similar to 26 nm sized crystallites which exhibited a pyroelectric coefficient as high as 15 nC cm(-2) K-1 which is in the same range (23 nC cm(-2) K-1) as that of single crystalline LiTaO3 at room temperature. The corresponding figures of merit that were calculated for the fast pulse detector (F-i), the large area pyroelectric detector (F-v) and the pyroelectric point detector (F-D) were 0.517 x 10(-10) m V-1, 0.244 m(2) C-1 and 1.437 x 10(-5) Pa-1/2, respectively. Glass nanocrystal composites comprising similar to 30 nm sized crystallites exhibited broad Maker fringes and the second harmonic intensity emanated from these was 0.5 times that of KDP single crystals.