The effect of ZnO on the sintering and stabilization of ZrO2 center dot MgO system

The sintering of ZrO2. MgO . ZnO powder has been investigated by TMA (Thermal Mechanical Analyser) and its phases analysed by XRD (X-ray diffraction pattern). The data obtained from sintering was studied by the Bannister equation and its dominant sintering mechanism was calculated. It was observed that the ZnO addition in the ZrO2. MgO solid solution lead to increased zirconia stabilization, According to the vacancies model, the ZnO addition did not lead to zirconia phases stabilization (PSZ). An analysis of the rate control in the initial stage of the sintering (region I) showed a mechanism of volume diffusion type. In other regions (regions II and III), the grain growth did lead to the Bannister equation deviation, which was observed by SEM (Scanning Electron Microscopy). These results were different from those demonstrated by other authors who studied the ZrO2. Y2O3 solid solution and obtained a mechanism of grain boundary diffusion type. (C) 1999 Published by Elsevier B.V. Ltd and Techna S.r.l. All rights reserved.

Surface damage of yttria-tetragonal zirconia polycrystals and magnesia-partially-stabilized zirconia in single-point abrasion

Commercially available 3Y-TZP and Mg-PSZ flats mere abraded by a 150 degrees diamond cone at -196 degrees, 25 degrees, 200 degrees, and 400 degrees C. The coefficient of friction, the track width, and the morphological features of the track were recorded. Raman spectroscopy mas used to record the tetragonal-to-monoclinic phase transformation (t --> m) as a function of distance away from the track. The study was undertaken to establish the influence of tangential traction on phase transformation and surface damage.

Performance of magnesia cements in porous blocks in acid and magnesium environments

The performance of porous blocks containing three different reactive magnesia-based cements - namely magnesia alone, magnesium oxide: Portland cement (PC) in 1:1 ratio, cured in ambient conditions, and magnesia alone, cured at elevated carbon dioxide conditions, in hydrochloric acid and magnesium sulfate solution - was investigated. Different aggressive chemical solution conditions were used, to which the samples were exposed for up to 12 months and then tested for strength and microstructure. The performance was also compared with that of standard PC-based blocks. The results showed the significant resistance to chemical attack offered by magnesia, both alone and with PC blend in the porous blocks when cured under ambient carbon dioxide conditions, and confirmed the much poorer performance of blocks made from PC alone. The blocks of solely magnesia cured in elevated carbon dioxide conditions, at 20% concentration, showed slightly lower resistance to acid attack than PC; however, the resistance to sulfate attack was much higher. © 2012 Thomas Telford Ltd.

Thermogravimetric study on the hydration of reactive magnesia and silica mixture at room temperature

The synthesis of magnesium silicate hydrate (MSH), which has wide applications in both construction and environmental fields, has been studied for decades. However, it is known that the characteristics of magnesia (MgO) vary significantly depending on their calcination conditions, which is expected to affect their performance in the MgO-SiO2-H2O system. This paper investigated the effect of different MgO and silica sources on the formation of magnesium silicate hydrate (MSH) at room temperature. The hydration process was studied by mixing commercial reactive MgO and silica powders with water and curing for 1, 7 and 28 days. The hydration products were analysed with the help of X-ray diffraction (XRD) and thermogravimatric analysis (TGA). The results showed the continuous consumption of MgO and the existence of MSH and brucite and other minor phases such as magnesite and calcite. It is found that the Mg and Si sources have significant effect on the hydration process of MgO-SiO2-H2O system. The reaction degree is controlled by the availability of dissolved Mg and Si in the solution. The former is determined by the reactivity of MgO and the latter is related to the reactivity of the silica as well as the pH of the system. © 2013 Elsevier B.V. All rights reserved.

Carbonating magnesia for soil stabilization

This paper investigates the potential for carbonating reactive magnesia (MgO) to serve as a more sustainable soil stabilization method by providing rapid and significant strength development of the stabilized soil through absorbing substantial quantities of CO2. Gaseous CO2 was forced through laboratory-prepared reactive MgO-treated soil samples in a triaxial cell set-up, and their resulting mechanical and microstructural properties were investigated using unconfined compressive strength, X-ray diffraction, and scanning electron microscopy. The results showed that adequately carbonated MgO-treated soils could, in a few hours, reach a similar strength range to corresponding 28 day Portland cement (PC)-stabilized soils. Hydrated magnesium carbonates, namely nesquehonite and hydromagnesite-dypingite, were the main products of the carbonated MgO in the soil, and were responsible for the significant strength development.