Lateral habits of single crystals of metallocene-catalyzed low molecular weight short chain branched polyethylene from the melt

The lateral habits of low molecular weight short chain branched polyethylene single crystals from the melt were studied. Three crystallization temperatures (102, 104 and 106 degrees C) were selected for single crystal growth. It was found that the lateral habits of single crystals were asymmetric at all the crystallization temperatures selected. The electron diffraction patterns and tilting series experiments evidenced that there existed chain tilting in all the lamellae. It was the chain tilting that lead to the asymmetry of the growth rate and of lateral habits of the single crystals about the b-axis. The lateral habits substantially changed from the growth at 102 degrees C where the truncated lozenge single crystals formed with straight (110) faces to the growth at 104 degrees C where the lenticular single crystals appeared. This change occurred at 20 degrees C lower than that in a low molecular weight linear polyethylene with the same molecular weight. Furthermore, kinetics theory analysis evidenced that the change of lateral habits from truncated lozenge to lenticular shape resulted from the transition of growth regime. The results were the same as that of high molecular weight linear polyethylene but different to that of low molecular weight linear polyethylene. It may be attributed by the existence of short branched chains. (C) 2000 Elsevier Science Ltd. All rights reserved.

Effects of pressure and molecular weight on the miscibility of polystyrene and cyclohexane

With the aid of Sanchez-Lacombe lattice fluid theory (SLLFT), the phase diagrams were calculated for the system cyclohexane (CH)/polystyrene (PS) with different molecular weights at different pressures. The experimental data is in reasonable agreement with SLLFT calculations. The total Gibbs interaction energy, g*(12) for different molecular weights PS at different pressures was expressed, by means of a universal relationship, as g(12)* =f(12)* + (P - P-0) nu*(12) demixing curves were then calculated at fixed (near critical) compositions of CH and PS systems for different molecular weights. The pressures of optimum miscibility obtained from the Gibbs interaction energy are close to those measured by Wolf and coworkers. Furthermore, a reasonable explanation was given for the earlier observation of Saeki et al., i.e., the phase separation temperatures of the present system increase with the increase of pressure for the low molecular weight of the polymer whereas they decrease for the higher molecular weight polymers. The effects of molecular weight, pressure, temperature and composition on the Flory Huggins interaction parameter can be described by a general equation resulting from fitting the interaction parameters by means of Sanchez-Lacombe lattice fluid theory.

Influence of short chain branches on crystallization and melting behavior of low molecular weight polyethylenes

The crystallization and melting behavior of mellocene-catalized branched and linear polyethylenes of low molecular weight was studied. It was found that the crystalline lattice of branched polyethylene is larger than that of linear polyethylene because of the existence of branched chains. The melting behavior of branched polyethylene is similar to that of linear polyethylene since the branched chains can not enter the lattice. However, the crystalline behavior of low molecular weight branched polyethylene is the same as that of high molecular weight linear polyethylene, but different with that of low molecular weigh linear polyethylene. Kinetics theory analysis evidenced that the transition temperature of growth regime of the branched polyethylene is about 20 degreesC lower than that of linear polyethylene with the same molecular weight. It may be attributed to the existence of short branched chains.

Determination of purity and molecular weight of calmodulin by matrix-assisted laser desorption/ionization time-of-flight mass spectrometry

The purity and molecular weight of calmodulin have been determined by means of matrix-assisted laser desorption/ionization time of flight mass spectrometry, and the results have been discussed. The experimental results demonstrate that this method is high sensitive and rapid as compared with other traditional methods.

Metallocene polyethylenes with broad or bimodal molecular weight distribution

Seven new binuclear titanocenes with different linking bridges, unsubstituted or substituted on the Cp rings, were synthesized and tested for their effect on ethylene polymerization in the presence of MAO. The polyethylenes thus obtained had broad MWD or even bimodal GPC curves, as compared with that from two reference mononuclear titanocenes. This is explained by the difference in degree of steric hindrance around the active center sites imposed by the bulky substituted ligands assuming different configurations in the rotation of the catalyst molecules. Lower polymerization temperatures alleviate the effect of these configuration differences, as reflected in change in MW and (M) over bar(w)/(M) over bar(n). This effect is not caused by decomposition or disproportionation of the binuclear titanocenes as evidenced by the stability of the catalyst.

Transport property of polyaniline and its molecular weight dependence

The electrical conductivity of polyaniline doped with camphor sulfonic acid (PAn-CSA) was studied. The results indicate that there is a critical temperature (T-c) and the temperature dependence of PAn-CSA conductivity shows metallic and semiconductor characteristics above and below T-c, respectively. The higher the molecular weight of PAn, the lower the T-c. The conductivity was enhanced remarkably when PAn-CSA film was stretched, its room temperature conductivity is up to 750 S/cm when elogonation is 60%; however, T-c was independent of elongation.

Impact behavior of phenolphthalein poly(ether sulfone) ultrahigh molecular weight polyethylene blends

This work presents the structure and impact properties of phenolphthalein poly(ether sulfone) blended with ultrahigh molecular weight polyethylene (PES-C/UHMWPE) at different compositions. The addition of UHMWPE can considerably improve the Charpy and Izod impact strength of the blends. The fracture surface is examined to demonstrate the toughening mechanics related to the modified PES-C resin. (C) 1998 John Wiley & Sons, Inc.

Mechanical and structural characteristics of phenolphthalein poly(ether sulfone) ultra-high molecular weight polyethylene blends

Mechanical and structural properties of blends of phenolphthalein poly(ether sulfone) (PBS-C) with ultra-high molecular weight polyethylene (UHMWPE) were investigated using tensile and bending testing, scanning electron microscopy and transition electron microscopy. The incorporation of minor amounts of UHMWPE (2 wt.-%) into PES-C has a reinforcement effect. With higher concentrations of UHMWPE, the mechanical properties decrease gradually. Structural studies demonstrated that the blends are multiphasic in the whole composition range. The minor UHMWPE, dispersed uniformly and oriented along the flow direction, as well as the strong interfacial adhesion contribute to the increase of the mechanical performance of the blends. The domain size of the UHMWPE phase was found to increase with the increase of its concentration.

Effects of molecular weight and interaction parameter on the glass transition temperature of polystyrene mixtures and its blends with polystyrene/poly(2,6-dimethyl-p-phenylene oxide)

The glass transition temperature (T-g) of mixtures of polystyrene (PS) with different molecular weight and of blends of poly(2,6-dimethyl-p-phenylene oxide) (PPO) and polystyrene with different molecular weight (DMWPS) was studied by a DSC method. For the whole range of composition, the curves of T-g vs composition obtained by experiment were compared with predictions from the Fox, Gordon-Taylor, Couchman and Lu-Weiss, equations. It was found that the experimental results were not in agreement with those from the Fox, Gordon-TayIor and Couchman equations for the binary mixtures of DMWPS, where the interaction parameter chi was approximately zero. However, for the blends PPO/DMWPS (chi < 0), with an increase of molecular weight of PS, it was shown that the experimental results fitted well with those obtained from the Couchman, Gordon-Taylor and Fox equations, respectively. Furthermore, the Gordon-Taylor equation was nearly identical to the Lu-Weiss equation when \chi\ was not very large. Further, the dependence of the change of heat capacity associated with the glass transition (Delta C-p) on the molecular weight of PS was investigated and an empirical equation was presented. (C) 1997 Elsevier Science Ltd.

Laser light scattering of the molecular weight distribution of unfractionated phenolphthalein poly(aryl ether sulfone)

Two unfractionated samples of phenolphthalein poly( aryl ether sulfone) (PES-C) were characterized in CHCl3 at 25 degrees C by applying a recently developed laser light-scattering (LLS) procedure. The Laplace inversion of precisely measured intensity-intensity time correlation function lead us first to an estimate of the characteristic line-width distribution G(Gamma) and then to the translational diffusion coefficient distribution G(D). A combination of static and dynamic LLS results enabled us to determine D = (2.69 x 10(-4))M(-0.553), which agrees with the calibration of D = (2.45 x 10(-4))M(-0.55) previously established by a set of narrowly distributed PES-C samples. Using this newly obtained scaling between D and M, we were able to convert G(D) into a differential weight distribution f(w)(M) for the two PES-C samples. The weight-average molecular weights calculated from f(w)(M) are comparable to that obtained directly from static LLS. Our results showed that using two broadly distributed samples instead of a set of narrowly distributed samples have provided not only similar final results, but also a more practical method for the PES-C characterization. (C) 1997 John Wiley & Sons, Inc.

The effect of formulated molecular weight on temperature resistance and mechanical properties in polyimide based composites

This experimental study examines the role of formulated molecular weight between crosslink sites on the temperature resistance and mechanical properties of composites based on a polyimide containing a diphenyl thioether unit (PTI). The composites are fabricated by in situ polymerization of monomer reactants (PMR) using three monomeric ingredients: bis(3,4-dicarboxyphenyl) sulfide dianhydride (TDPA); 4,4'-methylene dianiline (MDA); and the monomethyl ester of norbornene anhydride (NE). By changing monomeric molar ratio, three formulations are prepared, in which formulated molecular weight between crosslink sites varies from 1487 to 3446 g mol(-1). Unidirectional composite laminates from each formulation and T300 carbon fibres are compression moulded and cut into a series of test specimens. By measuring the glass transition temperature (T-g), Mode I interlaminar fracture toughness (G(IC)) and other mechanical properties at room and elevated temperatures, the influences of formulated molecular weight on the temperature resistance and mechanical properties of PTI-based composites are investigated.

Dynamic light-scattering characterization of the molecular weight distribution of a broadly distributed phenolphthalein poly(aryl ether ketone)

Using a recently developed laser light-scattering (LLS) procedure, we accomplished the characterization of a broadly distributed unfractionated phenolphthalein poly(aryl ether ketone) (PEK-C) in CHCl3 at 25 degrees C. The laplace inversion of precisely measured intensity-intensity time correlation function from dynamic LLS leads us first to an estimate of the characteristic line-width distribution G(Gamma) and then to the translational diffusion coefficient distribution G(D). By using a previously established calibration of D (cm(2)/s) = 2.37 X 10(-4)M(-0.57), were able to convert G(D) into a differential weight distribution f(w)(M). The weight-average molecular weight M(w) calculated from f(w)(M) agrees well with that directly measured in static LLS. Our results indicate that both the calibration and LLS procedure used in this study are ready to be applied as a routine method for the characterization of the molecular weight distribution of PEK-C. (C) 1996 John Wiley & Sons, Inc.

EFFECT OF IRRADIATION ON CRYSTALLINITY AND MECHANICAL-PROPERTIES OF ULTRAHIGH MOLECULAR-WEIGHT POLYETHYLENE

Ultrahigh molecular weight polyethylene (UHMWPE) has been irradiated (0-40 Mrad) with a Co-60 source at room temperature under vacuum. The crystallinity has been investigated by differential scanning calorimetry (DSC) and small-angle X-ray scattering (SAXS). The mechanical properties have been determined at room temperature. A significant increase of heat of fusion can be seen at low irradiation doses, which is attributed to crystallization, caused by chain scission during the process of irradiation. It is also observed that the thickness of the lamellae changes with irradiation dose. The Young's modulus has been improved significantly after irradiation at low doses. (C) 1993 John Wiley & Sons, Inc.

MOLECULAR-WEIGHT DEPENDENCE OF THE GLASS-TRANSITION OF CYCLIC POLYSTYRENE

The glass transition temperature (T(g)) of cyclic polystyrene was measured by differential scanning calorimetry. There was a marked difference in the glass transition behaviour between cyclic and linear polystyrene. In the low molecular weight region (M(n) < 5 x 10(3)), the T(g) of the cyclic polystyrene increased with decreasing M(n), contrary to that of linear polystyrene. With M(n) higher than 5 x 10(3), the T(g) of cyclic polystyrene increased with increasing M(n). The T(g) of cyclic and linear polystyrene approached the same constant value when the M(n) was high enough (M(n) > 10(5)). Combining the results of specific volume, it is believed that the variation of T(g) with molecular weight does not depend only on free volume effects but that configurational entropy is also an important factor.