Avaliação cinética e potencial do Nb2O5 obtido a partir de um complexo de nióbio para formação do oleato de metila através da reação de esterificação do ácido oleico

Among the heterogeneous catalysts materials made from niobium show up as an alternative to meet the demand of catalysts for biodiesel production. This study aims to evaluate the potential of a heterogeneous catalyst derived from a complex of niobium in the reaction of methyl esterification of oleic acid. The catalyst was synthesized after calcination at different temperatures of a niobium complex ((NH4)3[NbO(C2O4)3].H2O) generating a niobium oxide nanostructure with a different commercial niobium oxide used to synthesize the complex. The commercial niobium oxide, the complex niobium and niobium catalyst were characterized by thermogravimetry (TG and DTA), surface area analysis (BET), scanning electron microscopy (SEM) and X-ray diffraction (XRD), showing the catalyst has researched morphological and crystallographic indicating a catalytic potential higher than that of commercial niobium oxide characteristics. Factorial with central composite design point, with three factors (calcination temperature, molar ratio of alcohol/oleic acid and mass percentage of catalyst) was performed. Noting that the optimal experimental point was given by the complex calcination temperature of 600°C, a molar ratio alcohol/oleic acid of 3.007/1 and the catalyst mass percentage of 7.998%, with a conversion of 22.44% oleic acid in methyl oleate to 60 min of reaction. We performed a composite linear and quadratic regression to determine an optimal statistical point of the reaction, the temperature of calcination of the complex at 450°C, the molar ratio of alcohol/oleic acid 3.3408/1 and mass percentage of catalyst of 7.6833% . Kinetic modeling to estimate parameters for heterogeneous catalysis it set well the experimental results with a final conversion of 85.01% with 42.38% of catalyst and without catalyst at 240 min reaction was performed. Allowing to evaluate the catalyst catalytic studied has the potential to be used in biodiesel production

Preparação de catalisadores para reações de esterificação do ácido oleico baseados em matrizes polímericas sulfonadas POLI(1- FENILETILENO) (PS) e POLI(1-CLOROETILENO) (PVC)

Chemical modification of polymer matrices is an alternative way to change its surface properties. The introduction of sulfonic acid groups in polymer matrices alter properties such as adhesion, wettability, biocampatibility, catalytic activity, among others. This paper describes the preparation of polymeric solid acid based on the chemical modification of poly (1-fenietileno) (PS) and Poly (1-chloroethylene) (PVC) by the introduction of sulfonic acid groups and the application of these polymers as catalysts in the esterification reaction of oleic acid with methanol. The modified materials were characterized by Infrared Spectroscopy, Elemental Analysis and titration acid-base of the acid groups. All techniques confirmed the chemical changes and the presence of sulfur associated with sulfonic acid groups or sulfates. The modified polymers excellent performance in the esterification reaction of oleic acid with methanol a degree of conversion higher than 90% for all investigated polymers (modified PS and PVC (5% w / w)), with a mass ratio of oleic acid: methanol 1:10 to 100 ° C. The best performance was observed for the modified PVC catalyst (PVCS) which showed low degree of swelling during the reactions is recovered by filtration different from that observed for polystyrene sulfonate (PSS). Given these facts, the PVCS was employed as a catalyst in the esterification reaction of oleic acid in different times and different temperatures to obtain the kinetic parameters of the reaction. Experimental data show a great fit for pseudo-homogeneous model of second order and activation energy value of 41.12 kJ mol -1, below that found in the literature for the uncatalyzed reaction, 68.65 kJ mol -1 .The PVCS exhibits good catalytic activity for 3 times of reuse, with a slight decrease in the third cycle, but with a conversion of about 78%. The results show that solid polymeric acid has good chemical stability for the application in esterification reaction of commercial importance with possible application in the biodiesel production. The advantages in use of this system are the increased reaction rate at about 150 times, at these test conditions, the replacement of sulfuric acid as a catalyst for this being the most corrosive and the possibility of reuse of the polymer for several cycles.

Medidas de não-linearidades utilizando a técnica de varredura-Z aplicada a mistura ácido oleico e beta-caroteno

Neste trabalho utilizamos a técnica de varredura-Z para a determinação dos parâmetros ópticos não-lineares (índice de refração não-linear e coeficiente de absorção não-linear) do ácido oleico e das soluções de beta-caroteno diluído em ácido oleico. As concentrações das soluções estudadas foram as seguintes: 0, 5:6, 11:3, 22:5, 30, 45 e 60 μg=ml, os índices de refração foram calculados levando-se em consideração os dados experimentais e o modelo teórico previsto por Sheik-Bahae. As soluções de ácido oleico puro e de ácido oleico com beta-caroteno (60 μg=ml) apresentaram absorção não-linear e seus respectivos coeficientes foram calculados. Obtivemos também os índices de refração não-linear para os óleos de andiroba, buriti e copaíba, todos nativos da região Amazônica.

Avaliação in vitro da resistência adesiva ao cisalhamento entre a dentina bovina, cimentos resinosos e materiais restauradores indiretos, tratados ou não com jato de óxido de alumínio, ácido fluorídrico e silano

The purpose of this study was to evaluate in vitro the shear bond strenght to bovine dentin, during 24h and 30 days with the following variables: resin cements Enforce and Panavia F; aesthetics restorative materials Art Glass, IPS Empress 2 and Targis, with surface treatment with microetching with aluminium oxide, fluoridric acid and silane. Two hundred eighty eight sound bovine teeth from 3 years old animals constituted the samples after inclusion on polyester resin box. lnstron model 430 Universal Testing Machine, a crosshead speed 0,5 mm/min and load cells of 500 Kg, was used for shear bond strenght testing (MPa). The results were statistically analysed by ANOVA The best result was obtained with /PS Empress 2, microetched with aluminium oxide, fluoridric acid and silane, cemented with Panavia F and stored in distilled water, 3f'C during 30 days

Desenvolvimento de recobrimento submicrométrico de óxido de nióbio para aplicação em tubulações de prospecção de petróleo

Pós-graduação em Engenharia Mecânica - FEG

Estudos sobre a utilização de pentóxido de nióbio nanoestruturado na produção de biodiesel

In heterogeneous catalysis, numerous elements such as titanium and iron have been studied as nanoscale catalysts, but little is known about the use of niobium in nanocatalysis. The nanostructured particles have intrinsic and different physicochemical characteristics with great potential for use in industrial scale. Brazil having the largest known worldwide niobium reserve has the great challenge of creating pioneering technologies with the metal. Biodiesel is an alternative fuel and renewable substitute for regular diesel. Being biodegradable, non-toxic and have CO2 emissions lower than regular diesel, it contributes to the environment and to the independence from oil. The aim of this work was initially synthesize nanoscale particles of niobium pentoxide (Nanospheres, nanorods, nanofibers, nanocubes) from the sol-gel technique. The characterization of different nanoscale structures obtained was performed using different analytical techniques such as x-ray diffraction (XRD) and Scanning Electron Microscopy (SEM). The synthesized nanometer niobium oxide will be used as a heterogeneous catalyst in biodiesel synthesis from commercial soybean oil, checking in detail what the effect of morphology is presented (Nanospheres, nanorods, nanofibers, nanocubes) in the yield of biodiesel synthesis, comparing these results with those already described in literature for the amorphous niobium oxide and other oxide catalysts. The biodiesel obtained was characterized by gas chromatography system equipped with a FID detector

Resposta dos tecidos periodontais aos cimentos de silicato tricálcico associado ao óxido de zircônio ou óxido de nióbio usados no selamento de perfurações de furca em molares de ratos

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Resposta dos tecidos periodontais aos cimentos de silicato tricálcico associado ao óxido de zircônio ou óxido de nióbio usados no selamento de perfurações de furca em molares de ratos

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Comportamento da adição do carbeto de nióbio (nBC) na matriz metálica do aço ferrítico 15kH2mfa

The 15Kh2MFA steel is a kind of Cr-Mo-V family steels and can be used in turbines for energy generation, pressure vessels, nuclear reactors or applications where the range of temperature that the material works is between 250 to 450°C. To improve the properties of these steels increasing the service temperature and the thermal stability is add a second particle phase. These particles can be oxides, carbides, nitrites or even solid solution of some chemical elements. On this way, this work aim to study the effect of addition of 3wt% of niobium carbide in the metallic matrix of 15Kh2MFA steel. Powder metallurgy was the route employed to produce this metallic matrix composite. Two different milling conditions were performed. Condition 1: milling of pure 15Kh2MFA steel and condition 2: milling of 15Kh2MFA steel with addition of niobium carbide. A high energy milling was carried out during 5 hours. Then, these two powders were sintered in a vacuum furnace (10-4torr) at 1150 and 1250°C during 60 minutes. After sintering the samples were normalized at 950°C per 3 minutes followed by air cooling to obtain a desired microstructure. Results show that the addition of niobium carbide helps to mill faster the particles during the milling when compared with that steel without carbide. At the sintering, the niobium carbide helps to sinter increasing the density of the samples reaching a maximum density of 7.86g/cm³, better than the melted steel as received that was 7,81g/cm³. In spite this good densification, after normalizing, the niobium carbide don t contributed to increase the microhardness. The best microhardness obtained to the steel with niobium carbide was 156HV and to pure 15Kh2MFA steel was 212HV. It happened due when the niobium carbide is added to the steel a pearlitic structure was formed, and the steel without niobium carbide submitted to the same conditions reached a bainitic structure

Comportamento da adição do carbeto de nióbio (nBC) na matriz metálica do aço ferrítico 15kH2mfa

The 15Kh2MFA steel is a kind of Cr-Mo-V family steels and can be used in turbines for energy generation, pressure vessels, nuclear reactors or applications where the range of temperature that the material works is between 250 to 450°C. To improve the properties of these steels increasing the service temperature and the thermal stability is add a second particle phase. These particles can be oxides, carbides, nitrites or even solid solution of some chemical elements. On this way, this work aim to study the effect of addition of 3wt% of niobium carbide in the metallic matrix of 15Kh2MFA steel. Powder metallurgy was the route employed to produce this metallic matrix composite. Two different milling conditions were performed. Condition 1: milling of pure 15Kh2MFA steel and condition 2: milling of 15Kh2MFA steel with addition of niobium carbide. A high energy milling was carried out during 5 hours. Then, these two powders were sintered in a vacuum furnace (10-4torr) at 1150 and 1250°C during 60 minutes. After sintering the samples were normalized at 950°C per 3 minutes followed by air cooling to obtain a desired microstructure. Results show that the addition of niobium carbide helps to mill faster the particles during the milling when compared with that steel without carbide. At the sintering, the niobium carbide helps to sinter increasing the density of the samples reaching a maximum density of 7.86g/cm³, better than the melted steel as received that was 7,81g/cm³. In spite this good densification, after normalizing, the niobium carbide don t contributed to increase the microhardness. The best microhardness obtained to the steel with niobium carbide was 156HV and to pure 15Kh2MFA steel was 212HV. It happened due when the niobium carbide is added to the steel a pearlitic structure was formed, and the steel without niobium carbide submitted to the same conditions reached a bainitic structure

Esterificação direta de butenos com ácido acético em fase líquida

Este trabalho investiga o comportamento da reação de esterificação direta de butenos com ácido acético em fase líquida a partir de uma carga contendo butenos e butano. O estudo faz parte de um projeto que visa desenvolver uma rota alternativa para a produção do acetato de sec-butila, um solvente amplamente utilizado na indústria de tintas e vernizes e de elevado valor agregado. Foram testados três tipos de catalisadores para a reação de interesse: zeólitas, resinas de troca iônica e um catalisador a base de óxido de nióbio. As resinas mostraram-se mais eficientes sendo que, entre as resinas, aquela que apresentou maior conversão a acetato foi a resina Amberlyst 36 Dry. O estudo avaliou também a desativação do catalisador num tempo de aproximadamente 300h de operação a 90 ºC. Observou-se que, além do acetato de sec-butila, os principais sub-produtos formados foram o álcool sec-butílico, o éter butílico e oligômeros provenientes do buteno. Foram realizados experimentos a 50 ºC, 70 ºC, 90 ºC e 110 ºC com a razão molar inicial de ácido/buteno variando entre 0,6 e 2,6. Os testes foram conduzidos em um reator batelada com volume útil de um litro acoplado a um cromatógrafo, na ausência de efeitos difusivos. Foi proposto um modelo pseudo-homogêneo para descrever o comportamento da reação e foram estimadas as energias de ativação e os coeficientes pré-exponenciais das reações direta e inversa. A constante de equilíbrio termodinâmico também foi calculada, utilizando o modelo UNIFAC para a determinação dos coeficientes de atividade. Finalmente, os dados de equilíbrio foram comparados com os dados cinéticos, observando-se boa correlação principalmente para as temperaturas de trabalho mais altas.

Síntese de ésteres derivados do ácido oléico empregando lipases produzidas por Yarrowia lipolytica

Biodiesel é um biocombustível que consiste na mistura de ésteres monoalquílicos de ácidos graxos de cadeia longa. O processo usual de produção deste combustível é a transesterificação de óleos vegetais com álcoois de cadeia curta. Nesse processo, a matéria prima deve conter baixo conteúdo de ácido graxos livres ( ≤ 1%) e água (≤ 0,5%). Como alternativa ao processo de transesterificação, destaca-se o emprego de matérias-primas de baixo custo, com elevado teor de ácidos graxos livres, para a síntese de ésteres alquílicos através de reações de esterificação. As reações de produção do biodiesel podem ser catalisadas por via química (ácida e básica) ou enzimática. Na catálise enzimática, os biocatalisadores empregados são as lipases, que catalisam a hidrólise e síntese de ésteres e podem ser obtidas a partir de microrganismos, plantas ou tecido animal, sendo as de origem microbiana as mais utilizadas. O objetivo principal deste trabalho foi avaliar o potencial da lipase de Yarrowia lipolytica, uma levedura não convencional, na síntese de ésteres do ácido oleico visando à obtenção de ésteres alquílicos (biodiesel). Foram estudados os efeitos da temperatura (25, 30, 35, 40, 50 e 60oC), do teor enzimático (5, 10, 20, 30 e 40% v/v) e do tipo de álcool (metanol, etanol, n-propanol e n-butanol ) nas reações de esterificação do ácido oleico empregando o extrato enzimático líquido produzido por Yarrowia lipolytica. Os resultados obtidos mostraram que as reações conduzidas a 30oC e com 10% v/v do extrato enzimático apresentaram maior taxa inicial de reação. Também foi avaliada a utilização do extrato enzimático liofilizado (5% m/v) e do PES (produto enzimático sólido) (5% m/v) de Yarrowia lipolytica na reação de esterificação do ácido oleico com n-butanol a 30oC. O maior consumo de ácido oleico ocorreu na reação conduzida com o PES. O efeito da temperatura (25, 30, 35, 40 e 50oC) na síntese de oleato de butila foi, então, investigado nas reações empregando PES como biocatalisador e a maior conversão de ácido oleico foi verificada na temperatura de 40oC

Síntese e aplicação de catalisadores à base de óxidos de cério, tungstênio e HZSM-5 para a produção do biodiesel

This work presents a study on the production of biodiesel by esterification reaction of oleic acid with methanol using batch reactor and different catalysts based on CeO2 and WO3 and HZSM-5. Acid treatment was performed in order to increase the catalytic activity. Different characterization techniques were performed, among them X-ray diffraction (XRD), Thermogravimetric analysis TGA/DTA, Spectroscopy in the Region in Fourier Transform Infrared (FTIR) and X-ray fluorescence (XRF). The effects of independent variables: temperature, molar ratio of oil: alcohol and the amount of catalyst and their interactions on the dependent variable (conversion of oleic acid to the corresponding ester). Overall, through the results obtained in the characterization was observed that the applied treatments were efficient, however the XRF technique, indicated that tungsten oxide leaching could occur during the preparation of the materials. The treatments performed on HZSM-5 caused no significant changes in the structure indicating that the zeolite was quite resistant to the treatments used. It was evaluated using complete 23 factorial design. For the catalysts investigated, the best reaction conditions were obtained when using higher levels of the independent variables temperature and amount of catalyst. However, for the variable molar ratio the lowest level showed significant yields for most of the synthesized catalyst, obtaining maximum conversion to the OC (67.97%), OW (74.37%), HZSM-5 (61.16%) OC-OW 1 (75.93%), OC-OW 2 (82.57%), OC-OW 3 (79.15%), S/OC-OW 1 (86.90%), S/OC-OW 2 (91.04%), S/OC-OW 3 (88.60%), S/OC-OW/H 1 (92.34%), S/OC-OW/H 2 (100%) and S/OC-OW/H 3 (98.16%). According to the experimental design, the temperature has the biggest influence on the reaction variable for all the synthesized catalysts. Among the catalysts investigated S/OC-OW/H 2 e S/OC-OW/H 3 were more effective. Reuse tests showed that the catalyst activity decreased after each cycle, indicating that the regeneration process was effective. The leaching test indicated that the catalysts are heterogeneous in the evaluated operating range. The catalysts investigated showed themselves promising for the production of biodiesel.

Produção de biodiesel a partir da transesterificação de óleo de soja ácido por via enzimática

Neste trabalho, foi estudada a transesterificação enzimática do óleo de soja com álcool catalisada por lipase comercial imobilizada. Inicialmente foram investigados os efeitos da temperatura, do tipo de enzima (Novozym 435, Lipozyme RM-IM e Lipozyme TL-IM) e do tipo de álcool (etanol ou butanol) na síntese de biodiesel utilizando óleo de soja refinado. A melhor temperatura observada para as reações empregando Lipozyme TL IM e Lipozyme RM IM foi de 50C, enquanto que para a Novozym 435, a temperatura ótima foi de 70C. O maior teor em biodiesel (~60%) foi obtido na etanólise do óleo de soja a 70C utilizando Novozym 435 a 5% m/m. Também foi avaliada a síntese de biodiesel por via enzimática a partir da etanólise de óleos ácidos com índice de acidez (IA) (de 8,5, 54,4 e 93,7). A conversão do ácido graxo livre foi superior a 90% nas reações conduzidas com Novozym 435 nas reações com os três óleos ácidos testados. O teor em biodiesel foi próximo a 50% na etanólise do óleo de soja com índice de acidez de 8,5 empregando Lipozyme TL IM, porém para índices de acidez maiores este rendimento diminuiu. Para as reações conduzidas com Lipozyme RM-IM, o teor em biodiesel manteve-se em torno de 30% para todos os óleos ácidos investigados. A etanólise do óleo de soja refinado empregando reator de leito fixo em modo contínuo, a 50C, foi investigada variando a velocidade espacial dos reagentes (0,255 e 0,508 h-1), o tipo de lipase (Novozym 435, Lipozyme RM-IM e Lipozyme TL-IM) e a possibilidade de reuso do biocatalisador após lavagem com butanol. Na reação com Novozym 435, o teor em biodiesel foi de aproximadamente 50% e se manteve estável durante 4,5 h para as duas velocidades espaciais testadas. A lipase Lipozyme TL-IM apresentou teor em biodiesel maior do que o obtido nas reações com os outros biocatalisadores (~80%), porém não apresentou a mesma estabilidade. Foi observada uma queda significativa na produção de biodiesel nas reações empregando o reuso do biocatalisador

Catalisadores à base de Mg/La e de Al/La para a produção de biodiesel a partir de óleos refinados e ácidos

A crescente preocupação com a preservação do meio ambiente aliada às perspectivas de esgotamento das fontes de energia obtidas dos combustíveis fósseis tem impulsionado a indústria a desenvolver combustíveis alternativos a partir de recursos renováveis e processos ambientalmente não agressivos. O biodiesel, uma mistura de ésteres de ácidos graxos obtida pela transesterificação catalítica de óleos vegetais com álcoois de cadeia curta (metanol ou etanol) é um combustível alternativo importante, pelo fato das suas propriedades (índice de cetano, conteúdo energético e viscosidade) serem similares às do diesel obtido a partir do petróleo. No presente trabalho, a transesterificação do óleo de soja com metanol para a produção de biodiesel foi estudada em presença de catalisadores sólidos à base de Mg/La e Al/La com propriedades ácido-básicas. Catalisadores de Mg/La com uma relação molar Mg/La igual a 9:1 foram preparados por coprecipitação utilizando três métodos que se diferenciavam quanto ao tipo de agente precipitante e a temperatura de calcinação. O catalisador preparado com (NH4)2CO3/NH4OH como agente precipitante e calcinado a 450 C apresentou as melhores características físico-químicas e catalíticas. Catalisadores à base de Mg/La e Al/La com diferentes composições químicas foram sintetizados nas condições de preparo selecionadas. O comportamento catalítico destes materiais foi investigado frente à reação de transesterificação do óleo de soja com metanol. O catalisador de Al/La com uma relação molar Al/La igual a 9:1 mostrou o melhor desempenho catalítico (rendimento em ésteres metílicos igual a 84 % a 180 C) e pode ser reutilizado por pelo menos três ciclos de reação. Também foram realizados testes catalíticos na presença do óleo de soja com 10 % de ácido oleico verificando-se que os catalisadores utilizados possuem sítios capazes de catalisar as reações de transesterificação e esterificação