Influence of current density on crystalline structure and magnetic properties of electrodeposited Co-rich CoNiW alloys

The influence of current density, at the interval 5-100 mA cm-2, on the structural and magnetic properties of electrodeposited (Co 100-xNix)100-yWy alloys (x = 23-33.5 at. % Ni, y = 1.7-7.3 at. % W) was studied from a glycine-containing bath. W-content decreases with the increase of the current density magnitude. X-ray data have shown stabilization of hexagonal close packed, face centered cubic or a mixture of these structures by modulating the applied cathodic current density, for values lower than 50 mA cm-2. Two structural phase transitions were observed: one from hexagonal close packed to face centered cubic structural transition occurring for a current density of 20 mA cm -2, and another one, from cubic crystalline phase to amorphous state, which happens for values higher than 50 mA cm-2. These structural phase transitions seem to be associated with the W-content as well as average crystalline grain sizes that reduce with increasing the current density value. The grain size effect may explain the face centered cubic stabilization in Co-rich CoNiW alloys, which was initially assumed to be basically due to H-adsorption/incorporation. Magnetic properties of Co-rich CoNiW alloys are strongly modified by the current density value; as a result of the changes on the W-content and their structural properties© 2013 Elsevier B.V. All rights reserved.

Influence of stocking density on weight gain and behavior of feedlot lambs

The aim of this study was to verify the influence of the animal density on the weight gain and behavior of confined lambs. 86 animals were confined after weaning in 23 pens of two lambs each (double pens) and four pens of ten animals each (collective pens). During the 80 days of confinement all lambs received the same diet and the animals were weighed at the beginning of the trial and every 14 days for the control of the weight gain. The behavioral patterns were recorded by focal sampling method using a time sampling of 30 minutes, from 6:00 am to 6:00 pm, for 4 days. The behavioral variables were: posture (standing; lying), activity (eating; ruminating; leisure; drinking water; grooming) and events (nid-nodding; pushing; picking up; bellowing; mounting; defecating; urinating). For the evaluation of the weight gain and behavior of the animals an analysis of variance and multiple comparison procedure by Student t test was used. The average weight gain was higher for pen animals (0.228 kg/day) compared to the animals housed in the collective pens (0.208 kg/day; P = 0.07). A higher percentage of animals housed in double pens remained standing compared to the animals housed in collective pens at 8:30 am (P < 0.05), 11:30 am (P < 0.01), 2:30 pm (P < 0.01), 4:30 pm (P < 0.01), and 5:30 pm (P < 0.01). For the eating activity, it was observed that 6.9% more animals kept in the double pens remained in this activity at 8:30 am (P < 0.05) and 4:30 pm (P < 0.05), than in collective pen. No statistical difference was found for the other activities and events between treatments. The number of animals per group influenced the behavior of confined lambs, changing the pattern of food intake which could improve the weight gain. © 2013 Elsevier B.V. All rights reserved.

Influence of exercise order on upper body maximum and submaximal strength gains in trained men

The purpose of this study was to investigate the influence of exercise order on one-repetition maximum (1-RM) and ten-repetition maximum (10-RM) strength gains after 6 weeks of resistance training (RT) in trained men. Sixteen men were randomly assigned into two groups based on the order of exercises performed during training sessions: a group that performed large muscle group exercises first and progressed to small muscle group exercises (LG-SM); while a second group performed the opposite sequence and started with small muscle group exercises and progressed to large muscle group exercises (SM-LG). Four sessions of RT were conducted per week; all exercises were performed for three sets of 8-12 repetitions with 1-min rest intervals between sets. Maximal and submaximal strength were assessed at baseline and after 6 weeks of RT with 1-RM and 10-RM testing for the bench press (BP), lat pulldown (LPD), triceps pulley extension (TE) and biceps curl (BC), respectively. Two-way ANOVA for the 1-RM and 10-RM tests indicated a significant group x time interaction. The 1-RM values significantly increased for all exercises in both groups (P<0.05), but were not significantly different between groups. However, effect size (ES) data indicated that the LG-SM group exhibited a greater magnitude of gains (1-RM and 10-RM) for the BP and LPD exercises. Conversely, ES indicated that the SM-LG group exhibited a greater magnitude of gains (1-RM and 10-RM) for the TE and BC exercises. In conclusion, the results suggest that upper body movements should be prioritized and performed according to individual needs to maximize maximal and submaximal strength. © 2013 Scandinavian Society of Clinical Physiology and Nuclear Medicine.

Influence of filler charge on gloss of composite materials before and after in vitro toothbrushing

Objectives: This study evaluated the gloss behaviour of experimental resin composites loaded with different filler percentages, immediately after polishing and after toothbrushing simulation. Methods: Sixteen disc-shaped specimens were fabricated for each different-charged composite (40%, 50%, 60%, 70% and 75%) and polished with SiC abrasive papers. Gloss measurements were made prior to simulated toothbrushing. The specimens were subjected to the simulation for 5, 15, 30 and 60 min using an electrical toothbrush with a standardized pressure while being immersed in a toothpaste/artificial saliva slurry. Results: Baseline composite gloss values ranged from 69.7 (40%) to 81.3 (75%) GU (gloss units) and from 18.1 (40%) to 32.3 (75%) GU after 1 h of brushing. Highest gloss values were obtained by 75%-charged resin, while the lowest values were obtained by the 40%-charged one. Conclusions: All tested materials showed a gloss decrease. However, the higher filler load a composite resin has, the higher gloss it can achieve. Clinical significance: Gloss of resin composite materials is an important factor in determining aesthetic success of anterior restorations, and this property may vary according to the filler charge of the restorative material. Higher filler load of a composite resin results in higher gloss values. © 2013 Elsevier Ltd. All rights reserved.

Si-based thin film coating on Y-TZP: Influence of deposition parameters on adhesion of resin cement

This study evaluated the influence of deposition parameters for Si-based thin films using magnetron sputtering for coating zirconia and subsequent adhesion of resin cement. Zirconia ceramic blocks were randomly divided into 8 groups and specimens were either ground finished and polished or conditioned using air-abrasion with alumina particles coated with silica. In the remaining groups, the polished specimens were coated with Si-based film coating with argon/oxygen magnetron discharge at 8:1 or 20:1 flux. In one group, Si-based film coating was performed on air-abraded surfaces. After application of bonding agent, resin cement was bonded. Profilometry, goniometry, Energy Dispersive X-ray Spectroscopy and Rutherford Backscattering Spectroscopy analysis were performed on the conditioned zirconia surfaces. Adhesion of resin cement to zirconia was tested using shear bond test and debonded surfaces were examined using Scanning Electron Microscopy. Si-based film coating applied on air-abraded rough zirconia surfaces increased the adhesion of the resin cement (22.78 ± 5.2 MPa) compared to those of other methods (0-14.62 MPa) (p = 0.05). Mixed type of failures were more frequent in Si film coated groups on either polished or air-abraded groups. Si-based thin films increased wettability compared to the control group but did not change the roughness, considering the parameters evaluated. Deposition parameters of Si-based thin film and after application of air-abrasion influenced the initial adhesion of resin cement to zirconia. © 2013 Elsevier B.V. All rights reserved.

Influence of late treatment on how chronic myeloid leukemia responds to imatinib

ABSTRACT: INTRODUCTION: In Brazil, patients with chronic myeloid leukemia (CML) in the chronic phase were not given first-line imatinib treatment until 2008. Therefore, there was a long period of time between diagnosis and the initiation of imatinib therapy for many patients. This study aims to compare the major molecular remission (MMR) rates of early versus late imatinib therapy in chronic phase CML patients. METHODS: Between May 2002 and November 2007, 44 patients with chronic phase CML were treated with second-line imatinib therapy at the Hematology Unit of the Ophir Loyola Hospital (Belém, Pará, Brazil). BCR-ABL transcript levels were measured at approximately six-month intervals using quantitative polymerase chain reaction. RESULTS: The early treatment group presented a 60% probability of achieving MMR, while the probability for those patients who received late treatment was 40%. The probability of either not achieving MMR within one year of the initiation of imatinib therapy or losing MMR was higher in patients who received late treatment (79%), compared with patients who received early treatment (21%, odds ratio=5.75, P=0.012). The probability of maintaining MMR at 30 months of treatment was 80% in the early treatment group and 44% in the late treatment group (P=0.0005). CONCLUSIONS: For CML patients in the chronic phase who were treated with second-line imatinib therapy, the probability of achieving and maintaining MMR was higher in patients who received early treatment compared with those patients for whom the time interval between diagnosis and initiation of imatinib therapy was longer than one year.

Influence of whitening gel on pulp chamber temperature rise by in-office bleaching technique

INTRODUÇÃO: O clareamento dental representa uma manobra conservadora na recuperação estética de dentes com alterações cromáticas. Contudo, os tratamentos clareadores são passíveis de causar efeitos adversos, quando não bem planejados e executados. OBJETIVO: Este estudo avaliou a influência do gel clareador no aumento da temperatura intra-câmara pulpar através da técnica de clareamento dental fotoativado realizado em consultório. MATERIAL E MÉTODO: Um incisivo central superior humano foi seccionado na porção radicular 3 mm abaixo da junção cemento-esmalte. O canal radicular foi alargado para permitir a introdução do sensor do termômetro na câmara pulpar, a qual foi preenchida com pasta térmica, favorecendo a transferência de calor das paredes dentárias para o sensor do termômetro digital com termopar tipo K (MT- 401A) durante o clareamento. Três agentes clareadores fotossensíveis (peróxido de hidrogênio a 35%) foram utilizados, sendo: Whiteness HP (FGM), Whiteness HP Maxx (FGM) e Lase Peroxide Sensy (DMC). Um aparelho fotopolimerizador de led (Flash Lite - Discus Dental) foi empregado para a ativação dos géis clareadores. Seis ciclos de clareamento foram realizados para cada grupo testado. Os resultados foram submetidos à ANOVA de um critério e ao teste t (LSD) (α<0,05). RESULTADO: A menor média de variação de temperatura (ºC) foi observada com o Lase Peroxide Sensy (0,20), enquanto que a maior com o Whiteness HP (1,50). CONCLUSÃO: Os géis clareadores Whiteness HP e Whiteness HP Maxx interferiram significativamente no aumento da temperatura intra-câmara pulpar durante o clareamento, sendo esta variação dependente do tipo de gel clareador empregado.

Influence of creatine supplementation on indicators of glucose metabolism in skeletal muscle of exercised rats

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of Sm3+ doping on the dielectric properties of CaCu3Ti4O12 ceramics synthesized via autocombustion

Ca-1 -xSmxCu3Ti4O12 (x = 0.0, 0.2, 03) electronic ceramics were fabricated via the chemical route using metal nitrate solutions in order to improve the dielectric properties of this ceramic. X-ray diffraction (XRD) analysis indicated the formation of a single CaCu3Ti4O12 (CCTO). Grain size of the samples doped with Sm3+ was in the range of 1-2 mu m, as opposed to 50-100 mu m in the pure samples of CCTO. The cutoff frequency with the doping was remarkably shifted, from 1 MHz (pure CCTO) to 10 MHz (doped CCTO). Meanwhile, the real dielectric (epsilon(r)) and imaginary dielectric (epsilon '') constants showed a decrease as the doping was increased. (C) 2013 Elsevier B.V. All rights reserved.

Influence of the Extractant on the Complexing Capacity of Humic Substances from Peat for Macro and Micronutrients Using Continuous Flow: Agricultural Application and Environmental Impacts

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

The influence of insemination dose on pregnancy per fixed-time artificial insemination in beef cows is affected by semen extender

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The influence of bone quality on the biomechanical behavior of full-arch implant-supported fixed prostheses

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)