Preparation and properties of a novel nonionic surfactant grafted linear low density polyethylene

A novel nonionic surfactant, glycerol monostearic acid monomaleic acid diester (GMMD) was synthesized in our laboratory. Grafting-copolymerization of linear low density polyethylene (LLDPE) with GMMD was carried out by using P-ray irradiation in a twin-screw extruder. Evidence of the grafting of GMMD, as well as its extent, was determined by FT-IR. The effects of monomer concentration, reaction temperature and screw run speed on degree of grafting were studied systematically. The thermal behavior of LLDPE-g-GMMD was investigated by using differential scanning calorimety (DSC). Compared with neat LLDPE, the crystallization temperature (T,) of LLDPE-g-GMMD increased about 3 degrees C, and the melting enthalpy (Delta H-m) decreased with increase of GMMD content. It showed that the arafted GMMD monomer onto LLDPE acted as a nucleating agent. The tensile properties and light transmission of blown films were determined. Comparing with neat LLDPE film, no obvious changes could be found for the tensile strength, elongation at break and right angle tearing strength of LLDPE-g-GMMD film. Accelerated dripping property of film samples was investigated. The dripping duration of LLDPE-g-GMMD film and commercial anti-fog dripping film at 60 degrees C were 52 days and 17 days, respectively.

Robust core-shell supramolecular assemblies based on cationic vesicles and ring-shaped {Mo-154} polyoxomolybdate nanoclusters: Template-directed synthesis and characterizations

Substantial progress has been made recently in extending the supramolecular assembly of biomimetic structures to vesicle-based sophisticated nanocomposites and mesostructures. We report herein the successful preparation of unilamellar surfactant vesicles coated with a monolayer of ring-shaped {Mo-154} polyoxometalate (POM) nanoclusters, (NH4)(28)[Mo-154 (NO)(14)O(448)Hi(4)(H2O)(70)].approximate to 350H(2)O, by coulomb attractions using preformed didodecyldimethylammonium bromide (DDAB) surfactant vesicles as templates. The resultant vesicle-templated supramolecular assemblies are robust (they do not disintegrate upon dehydration) both at room-temperature ambient and vacuum conditions, as characterized by conventional transmission electron microscopy (TEM) and atomic force microscopy (AFM). The flexibility of the complex soft assemblies was also revealed by AFM measurements. The effect of POM-vesicle coulomb attractions on the dimensions of the templating vesicles was also investigated by using dynamic light scattering (DLS).Although origins of the structure stability of the as-prepared supramolecular assemblies are not clear yet, the nanometer scale cavities and the related properties of macroions of the POM clusters may play an important role in it.

In situ circular dichroic electrochemical study of bilirubin and bovine serum albumin complex

The electrooxidation of bilirubin (BR) and bovine serum albumin (BSA) complexes was studied by in situ circular dichroism (CD) spectroelectrochemistry. The result showed that the mechanism of the whole electrooxidation process of this complex corresponded to electrochemical processes (EE mechanism) in aqueous solution. Some parameters of the process were obtained by double logarithm method, differential method and nonlinear regression method. In visible region, CD spectra of the two enantiomeric components of the complex and their fraction distribution against applied potentials were obtained by singular value decomposition least-square (SVDLS) method. Meanwhile, the distribution of the five components of secondary structure was also obtained by the same method in far-UV region. The peak potential gotten from EE mechanism corresponds to a turning point for the component transition, beyond which the whole reaction reaches a new equilibrium. Under applied positive potentials, the enantiomeric equilibrium between M and P form is broken and M form transfers to its enantiomer of P, while the fraction of alpha-helix increases and that improves the transition to P form.

A new route to control product selectivity in the oxidative dehydrogenation of cyclohexane and cyclohexene

The product selectivity can be controlled by adding acetic acid in feed over vanadium phosphate (VPO) in gas phase oxidative dehydrogenation (ODH), in which cyclohexane and cyclohexene are oxidized to cyclohexene and 1,3-cyclohexadiene (1,3-CHD), respectively, at almost 100% selectivity. This approach is also an efficient method to capture the very unstable intermediates in the mechanism study.

Discrimination of herbal medicines by molecular spectroscopy and chemical pattern recognition

The molecular spectroscopy (including near infrared diffuse reflection spectroscopy, Raman spectroscopy and infrared spectroscopy) with OPUS/Ident software was applied to clustering ginsengs according to species and processing methods. The results demonstrate that molecular spectroscopic analysis could provide a rapid, nondestructive and reliable method for identification of Chinese traditional medicine. It's found that the result of Raman spectroscopic analysis was the best one among these three methods. Comparing with traditional methods, which are laborious and time consuming, the molecular spectroscopic analysis is more effective.

Growth and vibrational spectra of doped KMgF3 single crystal

The different ions doped KMgF3 single crystals are prepared by the vertical Bridgman method. The near-infrared absorption spectra for different parts of all as-growth crystals indicate that there is the best transparency in middle part. The correlation between the vibronic frequencies of Eu2+ and the site displacement of Cu+ co-doped ions is firstly studied, which indicates that Cu+ ions replace the site of the Mg2+ ions. The co-doped Eu2+ counteracts the charge misfit causing by the replacement of Mg2+ with Cu+. The overlapping of the emission spectra of the Eu2+ and the excitation spectra of the Cu+ results in the energy transfer from Eu2+ to Cu+.

Solvothermal synthesis of complex fluorides KCoF3 and KNiF3

Complex fluorides KCoF3 and KNiF3 with perovskite structures were solvothermally synthesized at 120-180 C and characterized by means of X-ray powder diffraction, scanning electron microscopy. thermogravimetric analysis and infrared spectroscopy.

Cardo polyarylethersulfones and polyaryletherketones bearing alkyl substituents on the phenylene unit

A series of cardo polyaryletherketones and polyaryletersulfones containing alkyl substituents of a different kind, number and volume were synthesized from bis(4-nitrophenyl)ketone or bis(4-fluorophenyl)sulfone with various alkyl substituted phenolphthaleins by polycondensation using K2CO3 as catalyst. Their chemical and aggregation structures were confirmed by FT-IR, H-1-NMR and WAXD. The resulting polymers were soluble in a variety of common polar solvents and, transparent, colorless, and tough films could be easily cast from 1,1,2-trichluoroethane solution. Their tensile strength, elongation at break and tensile modulis were in the range of 70.5 similar to 97.1MPa, 4.49%similar to7.81%, and 1.69 similar to2.27GPa, respectively. The prepared polymers had reasonably high glass transition temperatures at 207 to 269 degreesC, and showed fairly good thermal stability with 5% thermal decomposition loss above 410 degreesC.

Processible nanomaterials with high conductivity and magnetizability. Preparation and properties of maghemite/polyaniline nanocomposite films

A versatile process employing anionic surfactants has been developed for the preparation of processible nanocomposite films with electrical conductivity and magnetic susceptibility. Maghemite (g-Fe2O3) nanoclusters (similar to 10 nm in size) are coated with 4-dodecyl- benzenesulfonic acid, and polyaniline (PAn) chains are doped with 10-camphorsulfonic acid. The coated nanoclusters and doped polymers are soluble in common solvents, and casting the solutions readily gives free-standing nanocomposite films with nanocluster contents as high as similar to 50 wt %. The g-Fe2O3/PAn nanocomposites show high conductivity (82-337 S cm(-1)) and magnetizability (up to similar to 35 emu/g g-Fe2O3).

A new dinuclear molybdenum(V)-sulfur complex containing citrate ligand: synthesis and characterization of K2.5Na2NH4[Mo2O2S2(cit)(2)].5H(2)O

The complex, K2.5Na2NH4[Mo2O2S2(cit)(2)]. 5H(2)O (1), was obtained by crystallization from a solution of (NH4)(2)MoS4, potassium citrate (K(3)cit) and hydroxyl sodium in methanol and water under an atmosphere of pure nitrogen at ambient temperature. The crystals are triclinic, space group , a = 7.376 (3)Angstrom, b = 14.620 (2) Angstrom, c = 14.661 (1) Angstrom, alpha = 71.10 (1)degrees, beta = 81.77 (1)degrees, gamma = 78.27(2)degrees, R = 0.0584 for 2545 observed (I > 2 sigma (I)) reflections. Single crystal structure analysis reveals that citrate ligand coordinated to molybdenum atom through two carboxylato oxygens and one deprotonated hydroxyl oxygen together with two bridging sulfur atoms and a terminal oxygen atom completes distorted coordination octahedron around each molybdenum atom. Principal dimensions are: Mo = O-t, 1.707 Angstrom (av); Mo-S-b, 2.341 Angstrom (av); Mo-O-(hydroxyl), 2.021 Angstrom (av); Mo-O(alpha-carboxyl), 2.1290 Angstrom (av) and Mo-O(beta-carboxyl), 2.268(av) Angstrom. IR spectrum is in agreement with the structure.

Soluble and colorless polyimides from alicyclic diamines

A series of novel polyimides was synthesized from alicyclic diamines and various aromatic dianhydrides by one-step polymerization in m-cresol without a catalyst. The polymerization was conducted for 4 hours with refluxing, which was enough to obtain the polymers with high molecular weight. The inherent viscosities of the resulting polyimides were in the range of 0.30 similar to 1.29 dL/g. The prepared polyimides showed excellent thermal stabilities and good solubility. All the polymers were readily soluble in common organic solvents such as chloroform, tetrachloroethane (TCE), dimethylacetamide (DMAc), etc and the glass transition temperatures were observed at 199 to 311 degrees C. UV-visible spectra were obtained to measure the transparency of polymer films. All the polymers showed high transmission above 90% in the wavelength of 400 similar to 700 nm.

Studies on biodegradable poly(hexano-6-lactone) fibers 1. Structure and properties of drawn poly(hexano-6-lactone) fibers

Using high molecular weight (M-n=80,000) Poly(hexano-6-lactone) (PCL'), tough and high tenacity PCL monofilaments with various draw ratios (undrawn to 9 times drawn) were prepared by melt-spinning. The relationship between microstructure and properties of the PCL fibers is described in this current IUPAC Technical Report. Analysis of microstructure of the drawn PCL fibers by wide-angle X-ray diffraction revealed typical c-axis orientation with an increase in crystallinity. It was also supported by sonic velocity measurements. The thermal, mechanical, and dynamic mechanical properties of the PCL fibers were affected significantly by draw ratio. DSC thermograms showed that the melting temperature and the enthalpy of fusion increased with draw ratio. The temperature dependence curves of dynamic viscoelasticity showed that the temperature at tan delta peak of alpha dispersion corresponding to the glass transition temperature shifted toward higher temperature and the peak value of tan delta decreased with draw ratio. The dynamic storage modulus and the sonic modulus increased with draw ratio. These results are due to the increase in crystallinity and molecular orientation with drawing, and are responsible for an increase in tensile tenacity as well as knot tenacity of the PCL fibers.

Application of the Sanchez-Lacombe lattice fluid theory to the system pvme/ps and model calculations

Cloud point curves reported in the literature for five representatives of the system poly(vinyl methyl ether)/polystyrene were evaluated theoretically by means of the Sanchez-Lacombe lattice fluid theory. The measured phase separation behavior can be described within experimental error using only one adjustable parameter (quantifying the interaction between the unlike mers). The Flory-Huggins interaction parameters calculated from this theoretical description depend in good approximation linearly on composition (volume fractions) and on the inverse temperature. An evaluation of these data yields a maximum heat effect which is almost one order of magnitude less (ca. -0.25 J/cm(3)) than obtained via Hess's cycle (dissolution of the components and of the blend) from calorimetric measurements. Model calculations on the basis of the present theory demonstrate that the critical points shift to a different extent upon a certain relative change in the molar mass of the blend components. The sensitivity of the calculated phase diagrams against changes in the scaling parameter decreases in the following order: interaction energies between unlike mers, differences in the scaling temperatures, pressures and densities.