Preparation of bioactive glass ceramic nanoparticles by combination of sol-gel and coprecipitation method

SiO2-CaO-P2O5 ternary bioactive glass ceramic nanoparticles were prepared via the combination of sol-gel and coprecipitation processes. Precursors of silicon and calcium were hydrolyzed in acidic solution and gelated in alkaline condition together with ammonium dibasic phosphate. Gel particles were separated by centrifugation, followed by freeze drying, and calcination procedure to obtain the bioactive glass ceramic nanoparticles. The investigation of the influence of synthesis temperature on the nanopartilce's properties showed that the reaction temperature played an important role in the crystallinity of nanoparticle. The glass ceramic particles synthesized at 55 degrees C included about 15% crystalline phase, while at 25 degrees C and 40 degrees C the entire amorphous nanopowder could be obtained.

Internal Residual Stress Measurements in a Bioactive Glass-Ceramic Using Vickers Indentation

The residual stress distribution that arises in the glass matrix during cooling of a partially crystallized 17.2Na(2)O-32.1CaO-48.1SiO(2)-2.5P(2)O(5) (mol%) bioactive glass-ceramic was measured using the Vickers indentation method proposed by Zeng and Rowcliffe (ZR). The magnitude of the determined residual stress at the crystal/glass boundary was 1/4-1/3 of the values measured using X-ray diffraction (within the crystals) and calculated using Selsing`s model. A correction for the crack geometry factor, assuming a semi-elliptical shape, is proposed and then good agreement between experimental and theoretical values is found. Thus, if the actual crack geometry is taken into account, the indentation technique of ZR can be successfully used. In addition, a numerical model for the calculation of residual stresses that takes into account the hemispherical shape of the crystalline precipitates at a free surface was developed. The result is that near the sample surface, the radial component of the residual stress is increased by 70% in comparison with the residual stress calculated by Selsing`s model.

Influence of Bioactive Glass and/or Acellular Dermal Matrix on Bone Healing of Surgically Created Defects in Rat Tibiae: A Histological and Histometric Study

The purpose of this study was to histologically analyze the influence of bioactive glass and/or acellular dermal matrix on bone healing in surgically created defects in the tibiae of 64 rats (Rattus norvegicus, albinus, Wistar). Materials and Methods: A 4-mm X 3-mm unicortical defect was created on the anterolateral surface of the tibia. Animals were divided into 4 groups: C, control; BG, the defect was filled with bioactive glass; ADM, the defect was covered with acellular dermal matrix; and BG/ADM, the defect was filled with bioactive glass and covered with acellular dermal matrix. Animals were sacrificed at 10 or 30 days postoperatively, and the specimens were removed for histologic processing. The formation of new bone in the cortical area of the defect was evaluated histomorphometrically. Results: At 10 and 30 days postoperatively, groups C (39.65% +/- 5.63% / 63.34% +/- 5.22%) and ADM (38.12% +/- 5.53 / 58.96% +/- 7.05%) presented a larger amount of bone formation compared to the other groups (P<.05). In the same periods, groups BG (13.10% +/- 6.29% / 29.5% +/- 5.56%) and BG/ADM (20.72% +/- 8.31% / 24.19% +/- 6.69%) exhibited statistically similar new bone formation. However, unlike the other groups, group BG/ADM did not present a significant increase in bone formation between the 2 time points. Conclusion: Based on these results, it can be concluded that all of the materials used in this study delayed bone healing in non-critical-size defects. INT J ORAL MAXILLOFAC IMPLANTS 2008;23:811-817

Bioactive Glass for Alveolar Ridge Augmentation

The restoration and recovery of the alveolar healing process are a challenge to dental surgeons to achieve satisfactory results at the osseointegration of implants and implant rehabilitation. Different operative technique and biomaterials are being used to reconstruct the framework of the alveolar process. One of the biomaterials used for this purpose is the bioactive glass. The aim of this study was to report clinical and histologic final results of 7 clinical reports of alveolar ridge augmentation using bioactive glass. Clinically, bioglass was able to maintain bone architecture of the alveolar bone and repaired satisfactory. Biopsy was performed on the histologic samples and showed bone formation in intimate contact to the particles of the biomaterial.

Bone healing in critical-size defects treated with new bioactive glass/calcium sulfate: A histologic and histometric study in rat calvaria

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Histomorphometric analysis of tissue responses to bioactive glass implants in critical defects in rat calvaria

The aim of this study was to evaluate the osteogenic behavior of two chemically similar bioactive glass products (Biogran (R) and Perioglas (R)) implanted in critical bone defects in rat calvaria. Thirty-six transfixed bone defects of 8 mm diameter were made surgically in adult male Wistar rats. The animals were distributed equally into three groups: Biogran (GI), Perioglas (GII) and without implant material (control; GIII). The morphology and composition of both bioactive glasses were analyzed by scanning electron microscopy and energy-dispersive spectrometry. Tissue specimens were analyzed at the biological time points of 15, 30 and 60 days by optical microscopy and morphometry, demonstrating biocompatibility for the tested materials with moderate chronic inflammation involving their particles. Bone neoformation resulted only as a reparative reaction to an intentionally produced defect and was limited to the defect's edges. No statistically significant differences among the groups were observed. At the scar interstice, abundant deposits of collagenous fibers enveloping the particles were noted. The present results indicated that the bioactive glasses, under the experimental conditions analyzed, did not show osteogenic behavior. Copyright (c) 2007 S. Karger AG, Basel.

Effect of partial crystallization on the mechanical properties and cytotoxicity of bioactive glass from the 3CaO center dot P2O5-SiO2-MgO system

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Bone healing in surgically created defects treated with either bioactive glass particles, a calcium sulfate barrier, or a combination of both materials: A histological and histometric study in rat tibias

Objective: The purpose of this study was to histologically analyze the influence of bioactive glass and/or a calcium sulfate barrier on bone healing in surgically created defects in rat tibias. Material and methods: Sixty-four rats were divided into 4 groups: C (control), CS (calcium sulfate), BG (bioactive glass), and BG/CS (bioactive glass/calcium sulfate). A surgical defect was created in the tibia of each animal. In Group CS, a calcium sulfate barrier was placed to cover the defect. In Group BG the defect was filled with bioactive glass. In Group BG/CS, it was filled with bioactive glass and protected by a barrier of calcium sulfate. Animals were sacrificed at 10 or 30 days post-operative. The formation of new bone in the cortical area of the defect was evaluated histomorphometrically. Results: At 10 days post-operative, Group C presented significantly more bone formation than Groups CS, BG, or BG/CS. No statistically significant differences were found between the experimental groups. At 30 days post-operative, Group C demonstrated significantly more bone formation than the experimental groups. Groups CS and BG/CS showed significantly more bone formation than Group BG. No statistically significant differences were found between Group CS and BG/CS. Conclusions: (a) the control groups had significantly more bone formation than the experimental groups; (b) at 10 days post-operative, no significant differences were found between any of the experimental groups; and (c) at 30 days post-operative, the groups with a calcium sulfate barrier had significantly more bone formation than the group that used bioactive glass only. Copyright © Blackwell Munksgaard 2005.

Bone healing in critical-size defects treated with bioactive glass/calcium sulfate: A histologic and histometric study in rat calvaria

Objective: The purpose of this study was to analyze histologically the influence of bioactive glass (BG) with or without a calcium sulfate (CS) barrier on bone healing in surgically created critical-size defects (CSD) in rat calvaria. Material and methods: A CSD was made in each calvarium of 48 rats. They were divided into three groups: C (control): blood clot only; BG: defect filled with BG; and BG/CS: defect filled with BG covered by a CS barrier. Animals were euthanized at 4 or 12 weeks. Formation of new bone was evaluated histomorphometrically. Results: No defect completely regenerated with bone. BG particles were observed in Groups BG and BG/CS at both periods of analysis. The thickness throughout the healing area in Groups BG and BG/CS was similar to the original calvarium, while Group C presented a thin connective tissue in the center of the defect in both periods of analysis. At 4 weeks, Groups C and BG/CS presented significantly more bone formation than Group BG. No significant differences were found between Groups C and BG/CS. At 12 weeks, no significant differences in the amount of bone formation were observed among the three groups. When comparing 4 and 12 weeks, there was a significant increase in new bone formation within groups BG and BG/CS, but not C. Conclusion: BG particles, used with or without a CS barrier, maintained the volume and contour of the area grafted in CSD. However, they did not lead to a significant difference in bone formation when compared with control at 12 weeks post-operative. © 2007 Blackwell Munksgaard.

Repair of bone cavities in dog's mandible filled with inorganic bovine bone and bioactive glass associated with platelet rich plasma

The aim of this study was to evaluate the effect of platelet rich plasma (PRP) associated to bovine inorganic bone (Bio-Oss®; Geistlich) or bioactive glass (Bio-Gran®; Orthovita, Implant Innovations) on bone healing. Bone cavities were prepared in both sides of the mandible of 4 adult male dogs. The cavities were divided into 4 groups according to the filling material as follows: control, PRP, PRP/Bio-Oss, PRP/Bio-Gran. The animals were sacrificed after 120 days and histological and histomorphometrical analysis was performed. The control group showed 80.6% of bone formation in the longitudinal sections at 6 mm depth and 83.7% at 13 mm depth. The transverse sections displayed 74.2% at both 6 and 13 mm depths. The PRP group showed 21.1% of bone formation in the longitudinal sections at 6 mm depth, and 23.1% at 13 mm depth. The transverse sections presented 28.98% of bone formation at 6 mm depth and 41.2% at 13 mm depth. The PRP/Bio-Gran group showed 25.1% of bone formation in the longitudinal sections at 6 mm depth and 30.4% at 13 mm depth. In the transverse sections, the bone formation was 43.0% at 6 mm depth and 39.7% at 13 mm depth. The PRP/Bio-Oss group showed 35.5% of bone formation in the longitudinal sections at 6 mm depth and 42% at 13 mm depth. In the transversal sections, the bone formation was 26.8% and 31.2% at the depths of 6 and 13 mm, respectively. PRP alone or associated with bovine inorganic bone or bioglass had no significant effect in bone healing.

Influência da adição de bioactive glass na liberação de íons do cimento de ionômero de vidro modificado por resina

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Filling of extraction sockets of feline maxillary canine teeth with autogenous bone or bioactive glass

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)