Synthesis of M2AC (M = Ti, V, Cr, Nb, Zr, A = Al, Sn, S) (MAX) carbide phases and study of their physical behavior under extreme conditions

Materials known as Mn+1AXn phases, where n is 1, 2, or 3, and M represents an early transition metal, A an A-group element, and X is either Carbon and/or Nitrogen [1], are fast becoming technologically important materials due to the interesting combination of unique properties. However, a lot of important information about the high temperature and high pressure behavior of many of these compounds is still missing, which needs to be determined systematically. ^ In this dissertation the synthesis of M2AC (M = Ti, V, Cr, Nb, Zr) and A = (Al, Sn, S) compounds by arc melting, vacuum sintering and piston cylinder synthesis is presented along with the synthesis of Zr 2SC, which has been synthesized for first time in bulk form, by piston cylinder technique. The microstructural analysis by electron microscopy and phase analysis by x-ray diffraction is presented next. Finally, a critical analysis of the behavior of these compounds under the application of extreme pressure (as high as 50 GPa) and temperature (≈ 1000°C) is presented. ^ The high pressure studies, up to 50 GPa, showed that these compounds were structurally intact and their bulk moduli ranged from 140 to 190 GPa. The high temperature studies in the inert atmosphere showed that the M 2SnC compounds were unstable above 650°C and the expansion along the a-axis was higher than that along the c-axis, unlike the other phases. M2SC compounds on the other hand showed negligible difference in the thermal expansion along the two axes. The oxidation study revealed that Ti2AC (Al, S) compounds had highest resistance to oxidation while the M2SnC compounds had the least. Furthermore, from the oxidation study of these compounds, which were short time oxidation experiments, it was found that all of these compounds oxidized to their respective binary oxides. ^

Synthesis of copper carbon nanotube composite and its electrical conductivity measurement

The matrices in which Multi Walled Carbon Nanotubes (MWCNTs) are incorporated to produce composites with improved electrical properties can be polymer, metal or metal oxide. Most composites containing CNTs are polymer based because of its flexibility in fabrication. Very few investigations have been focused on CNT-metal composites due to fabrication difficulties, such as achievement of homogeneous distribution of MWCNTs and poor interfacial bonding between MWCNTs and the metal matrix. In an effort to overcome poor interfacial bonding for the Cu - MWCNT composite, silver (Ag) and nickel (Ni) resinates have been incorporated in the ball milling stage. Composites of MWCNT (16, 12, and 8 Vol %) - Cu+Ag+Ni were pelleted at 20,000 psi (669.4 Mpa) and sintered at 950 °C. The electrical conductivity results measured by four probe meter showed that the conductivity decreases with increase in the porosity. Moreover from these results it can also be stated that an addition of optimum value of (12 Vol %) MWCNT leads to high electrical conductivity (9.26E+07 s-m"), which is 50% greater than the conductivity of Cu. It is anticipated that the conductivity can be increased substantially with hot isostatic pressing of the pellet.