Responsive core−shell latex particles as colloidosome microcapsule membranes

Responsive core-shell latex particles are used to prepare colloidosome microcapsules using thermal annealing and internal cross-linking of the shell, allowing production of the microcapsules at high concentrations. The core-shell particles are composed of a polystyrene core and a shell of poly[2-(dimethylamino)ethyl methacrylate]-b-poly[methyl methacrylate] (PDMA-b-PMMA) chains adsorbed onto the core surface, providing steric stabilisation. The PDMA component of adsorbed polymer shell confers the latex particle thermal and pH responsive characteristics, it also provides glass transitions at lower temperatures than that of the core and reactive amine groups. These features facilitate the formation of stable Pickering emulsion droplets and the immobilisation of the latex particle monolayer on these droplets to form colloidosome microcapsules. The immobilisation is achieved through thermal annealing or cross-linking of the shell at mild conditions feasible for large scale economic production. We demonstrate here that it is possible to anneal the particle monolayer on the emulsion drop surface at 75-86 ºC by using the lower glass transition temperature of the shell compared to that of the polystyrene cores (~108 ºC). The colloidosome microcapsules formed have a rigid membrane basically composed of a monolayer of particles. Chemical cross-linking has also been successfully achieved by confining a cross-linker within the disperse droplet. This approach leads to the formation of single-layered stimulus-responsive soft colloidosome membranes and provides the advantage of working at very high emulsion concentrations since inter-droplet cross-linking is thus avoided. The porosity and mechanical strength of microcapsules are also discussed here in terms of the observed structure of the latex particle monolayers forming the capsule membrane.

Autonomous volume transitions of a polybase triblock copolymer gel in a chemically driven pH-oscillator

A pH-responsive ABA triblock copolymer, comprising poly(methyl methacrylate)-b/ock-poly(2-(diethylamino)ethyl methacrylate)-block-poly(methyl methacrylate) [PMMA-b-PDEA-b-PMMA], has been cast Into thin films with a well-defined microstructure. Small Angle X-ray Scattering (SAXS) and Atomic Force Microscopy (AFM) studies confirm that this copolymer forms a hydrogel consisting of PMMA spheres embedded within a polybase PDEA matrix, with the PMMA domains acting as physical cross-links. The hydrogel has a pH-reversible coil-globule transition at around pH 4.5. This responsive physical property was exploited by immersing a sample of copolymer hydrogel in an aqueous solution containing a cyclic pH-oscillating reaction, whereby the pH was continuously oscillated above and below the transition pH so as to induce autonomous volume transitions. The changes in microscopic and macroscopic length scales correlate closely during (de)swelling cycles, with affine behaviour occurring over five orders of magnitude. Copyright © 2007 WILEY-VCH Verlag GmbH & Co. KGaA,.

Electrospinning pH-responsive block copolymer nanofibers

Electrospinng of a fibrous triblock copolymer consisting of poly(methyl methacrylate-block-poly[2-(diethylamino) ethyl methacrylate]-block-poly(methyl methacrylate) (PMMA-b-PDEA-b-PMMA) has been discussed. A mixed co-solvent system of tetrahydrofuran (THF) and dimethylformamide (DMF) was used to electrospin fibrous PMMA-b-PDEA-b-PMMA and its influence on surface morphology and diameter of the electrospun fiber was also investigated in an attempt to control the fiber diameter. The concentration range between 20 and 40 wt % was found suitable for electrospinning of PMMA-b-PDEA-b-PMMA in a THF/DMF system. It was also observed that the average fiber diameter decreased as the content of DMF was increased. A significant decrease in fiber diameter was observed when moving from a THF solution to a THF/DMF system at a ratio of 70:30.

The performance of poly(styrene)-block-poly(2-vinyl pyridine)-block- poly(styrene) triblock copolymers as pH-driven actuators

Poly(styrene)-block-poly(2-vinyl pyridine)-block-poly(styrene) (PS-b-P2VP-b-PS) triblock copolymers were synthesised by anionic polymerisation. Thick films were cast from solution and their structure analysed by small angle X-ray scattering (SAXS). Longer annealing times led to more ordered structures whereas short evaporation times effectively "lock" the polymer chains in a disordered state by vitrification. Well-ordered structures not only provide an isotropic network, which reduces localised stress within the material, but are also essential for fundamental studies of soft matter because their activity on the molecular scale must be analysed and understood prior to their use in technological applications. Well-characterised PS-b-P2VP-b-PS materials have been coupled to a pH-oscillating reaction and their potential application as responsive actuators is discussed. This journal is © The Royal Society of Chemistry.