Enhanced (1)G(4) emission in NaLaF4: Pr3+, Yb3+ and charge transfer in NaLaF4: Ce3+, Yb3+ studied by fourier transform luminescence spectroscopy

A high resolution luminescence study of NaLaF4: 1%Pr3+, 5%Yb3+ and NaLaF4: 1%Ce3+, 5%Yb3+ in the UV to NIR spectral range using a InGaAs detector and a fourier transform interferometer is reported. Although the Pr3+(P-3(0) -> (1)G(4), Yb3+(F-2(7/2) -> F-2(5/2)) energy transfer step takes place, significant Pr3+ (1)G(4) emission around 993, 1330 and 1850 nm is observed. No experimental proof for the second energy transfer step in the down-conversion process between Pr3+ and Yb3+ can be given. In the case of NaLaF4: Ce3+, Yb3+ it is concluded that the observed Yb3+ emission upon Ce3+ 5d excitation is the result of a charge transfer process instead of down-conversion. (C) 2010 Elsevier B.V. All rights reserved.

Highly Efficient IR to NIR Upconversion in Gd2O2S: Er3+ for Photovoltaic Applications

Upconversion (UC) is a promising option to enhance the efficiency of solar cells by conversion of sub-bandgap infrared photons to higher energy photons that can be utilized by the solar cell. The UC quantum yield is a key parameter for a successful application. Here the UC luminescence properties of Er3+-doped Gd2O2S are investigated by means of luminescence spectroscopy, quantum yield measurements, and excited state dynamics experiments. Excitation into the maximum of the 4I15/2 → 4I13/2 Er3+ absorption band around 1500 nm induces very efficient UC emission from different Er3+ excited states with energies above the silicon bandgap, in particular, the emission originating from the 4I11/2 state around 1000 nm. Concentration dependent studies reveal that the highest UC quantum yield is realized for a 10% Er3+-doping concentration. The UC luminescence is compared to the well-known Er3+-doped β-NaYF4 UC material for which the highest UC quantum yield has been reported for 25% Er3+. The UC internal quantum yields were measured in this work for Gd2O2S: 10%Er3+ and β-NaYF4: 25%Er3+ to be 12 ± 1% and 8.9 ± 0.7%, respectively, under monochromatic excitation around 1500 nm at a power of 700 W/m2. The UC quantum yield reported here for Gd2O2S: 10%Er3+ is the highest value achieved so far under monochromatic excitation into the 4I13/2 Er3+ level. Power dependence and lifetime measurements were performed to understand the mechanisms responsible for the efficient UC luminescence. We show that the main process yielding 4I11/2 UC emission is energy transfer UC.

Origin of the high upconversion green luminescence efficiency in -NaYF4:2% Er3+,20% Yb3+

Site-selective spectroscopy in hexagonal beta-NaYF4:Er3+,Yb3+ has revealed different environments for Er3+ ions (multisite formation). The low-temperature S-4(3/2) -> (I15/2Er3+)-I-4 green emission depends on the excitation wavelength associated with the F-4(7/2) Er3+ level. We have studied the effect of hydrostatic pressure on the green, red, and blue Er3+ emission upon NIR excitation at similar to 980 nm, in order to establish the role played by energy resonance conditions and the multiple Er3+ sites due to the disordered structure for the upconversion (UC) process (energy tuning). The variation of photoluminescence spectra and lifetimes as a function of pressure and temperature reveals that the origin of the high green UC efficiency of the beta-NaYF4:Er3+,Yb3+ compound is mainly due to the multisite distribution, and the low phonon energy of the host lattice.

Luminescence Enhancement after Adding Stoppers to Europium(III) Nanozeolite L

Stopper molecules attached to nanozeolite L (NZL) boost the luminescence of confined Eu3+-β-diketonate complexes. The mechanism that is responsible was elucidated by comparing two diketonate ligands of different pKa and two aromatic imines, and by applying stationary and time resolved spectroscopy. The result is that the presence of the imidazolium based stopper is favorable to the sustainable formation of Eu3+-β-diketonate complexes with high coordination by decreasing the proton strength inside the channels of NZL. A consequence is that strongly luminescent transparent films can be prepared using aqueous suspension of the stopper modified composites.