Post consumer pet depolymerization by acid hydrolysis

The reaction of post-consumer poly(ethylene terephthalate) with aqueous solutions of sulfuric acid 7.5M was investigated in terms of temperature, time and particle size. The reaction extent reached 80% in four days at 100 degrees C and 90% in 5 hours at 135 degrees C. TPA obtained was purified and considered in the same level of quality of the commercial one after tests of elemental analysis, particle size and color. It was concluded that the hydrolysis occurred preferentially at the chain ends and superficially, having as controller mechanism the acid diffusion into the polymer structure. The shrinking-core model can explain the reaction kinetics.

Additional steps in mechanical recyling of PET

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Characterization of Post-Consumer PET after Removal of the Original Surface: Influence of Raw Material

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Openability of soft drinks PET packagings

Studies on packaging accessibility are still incipient in Brazil. Many of these packagings can represent a challenge to users, whether due to non-informative labels, tricky tabs or seals, or even those that need strength to open. This paper brings a simple test to determine the necessary torque force to open PET bottles, and to predict the amount of users that could not open it. The findings suggest that a considerable amount of users could not open it or would have some difficulties to exert the necessary force.

Migration of Tinuvin P, a UV stabilizer, from PET bottles into fatty-food simulants

Tinuvin P migration from Polyethyleneterephthalate (PET) bottles was investigated using several fatty-food simulants such as olive oil, soybean oil, n-heptane and iso-octane, at exposure conditions of 2-10 days at 40 degrees C (total immersion). The stability of several UV stabilizers (BHT, Cyasorb UV 5411, Tinuvin P, Tinuvin 326 and Tinuvin 327) in n-heptane and iso-octane was also studied. After 10 days at 40 degrees C, losses of 6% and 20% in iso-octane and n-heptane respectively, were verified for Tinuvin P. Other UV stabilizers at the same experimental conditions showed higher losses (up to 30% for Tinuvin 327). These results confirm that, when carrying out specific migration studies, the stability of the substance of interest should be established in the food simulant to avoid underestimating the real migration behaviour. In order to quantify UV stabilizer migration, n-heptane and iso-octane solutions were concentrated and directly analysed by SIM mode GC-MS. For olive and soybean oils, Tinuvin P was isolated using size-exclusion chromatography and quantified by SIM mode GC-MS. Iso-octane proved to be a move suitable fatty-food simulant than n-heptane for the migration study of Tinuvin P from PET. Higher levels of Tinuvin P migrated to olive and soybean oils rather than to n-heptane. These results suggest that the MERCOSUL recommended official methods for specific migration studies should be revised since the migration levels using n-heptane as a fatty-food simulant could be underestimated when compared to edible oils. Copyright (C) 1999 John Wiley & Sons, Ltd.

Efeitos da história térmica nas propriedades do polímero pet: um experimento para ensino de análise térmica

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

PET containers in Brazil: Opportunities and challenges of a logistics model for post-consumer waste recycling

The use of post-consumer materials is directly related to reducing the cost of production and extraction of natural resources. Non-recyclable materials are randomly disposed in the environment. Brazil is one of the largest consumers of PET (polyethylene terephthalate) bottles. The purpose of this paper is to describe the opportunities and challenges of the logistics model for post-consumer PET bottle recycling in Brazil, while providing knowledge of its practices along the recycling chain. The results describe the need to educate those directly and indirectly involved in the process: to reduce consumption in order to reduce the amount of waste generated: to structure the post-consumer reverse chain and engage industrial sectors and government, through public policies, to support cleaner technologies along the PET bottle production chain. (C) 2010 Elsevier B.V. All rights reserved.

Surface energy increase of oxygen-plasma-treated PET

Prosthetic composite is a widely used biomaterial that satisfies the criteria for application as an organic implant without adverse reactions. Polyethylene therephthalate (PET) fiber-reinforced composites have been used because of the excellent cell adhesion, biodegradability and biocompatibility. The chemical inertness and low surface energy of PET in general are associated with inadequate bonds for polymer reinforcements. It is recognized that the high strength of composites, which results from the interaction between the constituents, is directly related to the interfacial condition or to the interphase. A radio frequency plasma reactor using oxygen was used to treat PET fibers for 5, 20, 30 and 100 s. The treatment conditions were 13.56 MHz, 50 W, 40 Pa and 3.33 x 10(-7) m(3)/s. A Rame-Hart goniometer was used to measure the contact angle and surface energy variation of fibers treated for different times. The experimental results showed contact angle values from 47degrees to 13degrees and surface energies from 6.4 x 10(-6) to 8.3 x 10(-6) J for the range of 5 to 100 s, respectively. These results were confirmed by the average ultimate tensile strength of the PET fiber/polymethylmethacrylate (PMMA) matrix composite tested in tensile mode and by scanning electron microscopy. (C) 2003 Elsevier B.V. All rights reserved.

Treatment of PET and PU polymers by atmospheric pressure plasma generated in dielectric barrier discharge in air

Plasma treatments are frequently employed to modify surface properties of materials such as adhesivity, hydrophobicity, oleophobicity etc. Present work deals with surface modification of common commercial polymers such as polyethylene terephthalate (PET) and polyurethane (PU) by an air dielectric barrier discharge (DBD) at atmospheric pressure. The DBD treatment was performed in a plain reactor in wire-duct geometry (non-uniform field reactor), which was driven by a 60 Hz power supply. Material characterization was carried out by water contact angle measurements, atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS). The plasma-induced modifications are associated with incorporation of polar oxygen and nitrogen containing groups on the polymer surface. The AFM analysis reveals that the plasma treatment roughens the material surface. Due to these structural and morphological changes the surface of DBD-treated polymers becomes more hydrophilic resulting in enhanced adhesion properties. (C) 2010 Elsevier B.V. All rights reserved.

Carbon dioxide formation during initial stages of photodegradation of poly(ethyleneterephthalate) (PET) films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of cold plasma treatment on mechanical properties of PET/PMMA composites

Mechanical strength of polyethylene terephthalate (PET) fibres and polymethyl methacrylate (PMMA) matrix composites were studied with particular interest on the effects of oxygen and argon plasma treated fibres. PET. fibres were treated in a radio frequency plasma reactor using argon or oxygen for different treatment times to increase the interface adhesion. Fibre volume fraction was measured through digital image analysis. Elastic moduli resulted between 3 GPa for untreated to 6 GPa for treated composites. Tensile tests on PET fibres showed that plasma treatment caused a decrease in average tensile strength compared to untreated fibres. Fracture analysis confirmed the increase in interfacial adhesion due to plasma treatment. (c) 2004 Elsevier Ltd. All rights reserved.

Tensile strength of radio frequency cold plasma treated PET fibers - Part 1: Influence of environment and treatment time

This article reports on a series of experiments with polyethylene terepthalate (PET) treated in a radio frequency plasma reactor using argon and oxygen as a gas fuel, for treatment times equal to 5 s, 20 s, 30 s, and 100 s. The mechanical strength modification of PET fibers, evaluated by tensile tests on monofilaments, showed that oxygen and argon plasma treatment resulted in a decrease in the average tensile strength compared with the untreated fibers. This reduction in tensile strength is more significant for argon plasma and is very sensitive to the treatment time for oxygen plasma. Scanning electron microscopy (SEM) used to analyze the effects of cold plasma treatment on fiber surfaces indicates differences in roughness profiles depending on the type of treatments, which were associated with variations in mechanical strength. Differences in the roughness profile, surveyed through an image analysis method, provided the distance of roughness interval, D-ri. This parameter represents the number of peaks contained in a unit length and was introduced to correlate fiber surface condition, before and after cold plasma treatments, and average tensile strength. Statistical analysis of experimental data, using Weibull cumulative distribution and linear representation, was performed to explain influences of treatment time and environmental effects on mechanical properties. The shape parameter, alpha, and density parameter, beta, from the Weibull distribution function were used to indicate the experimental data range and to confirm the mechanical performance obtained experimentally.

Calorimetric and SEM studies of PHB-PET polymeric blends

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Fibre analysis and fibre digestibility in pet foods - a comparison of total dietary fibre, neutral and acid detergent fibre and crude fibre

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Comparison between different conditions of the chemical polymerization of polyaniline on top of PET films

Composites produced during the in situ chemical polymerization of aniline on top of a poly(ethylene terephthalate) (PET) film, in different conditions, were studied by open-circuit potential (Voc), ultraviolet-visible, and infrared spectroscopy, electrical conductivity measurements, scanning electron microscopy, and atomic force microscopy. The polymerization monitoring by Voc showed a maximum associated with the intermediate pernigraniline oxidation state and a final formation of polyaniline (PANI) in the doped emeraldine salt (ES) form. Furthermore, high electrical conductivity values were obtained for the PANI-ES coating prepared under selected conditions. A globular formation was observed for the doped PANI-ES coating with globules of sizes of the same order and same shape of the PET, demonstrating the influence of the substrate on the coating morphology.