Ionothermal synthesis of the mixed-anion material, Ba3Cl4CO3

A low-temperature ionothermal method for the facile synthesis of the halide carbonate, Ba3Cl4CO3, in single-crystalline form has been developed. This has enabled the first determination of the crystal structure of this material to be carried out. Analysis of single-crystal X-ray diffraction data indicates that barium chloride carbonate crystallises in the orthorhombic space group Pnma (Z=4), with a=8.4074(11), b=9.5886(12), c=12.4833(15) Å (Rw=0.0392). It exhibits a complex structure in which a three-dimensional network is formed from cross-linking of chains of anion-centred octahedra that share faces.

Efficiency and purity control in the preparation of pure and/or aluminum-doped barium ferrites by hydrothermal methods using ferrous ions as reactants

The synthesis of hexagonal barium ferrite (BaFe12O19) was studied under hydrothermal conditions by a method in which a significant amount of ferrous chloride was introduced along side ferric chloride among the starting materials. Though all of the Fe2+ ions in the starting material were converted to Fe3+ ions in the final product, Fe2+ was confirmed to participate differently from the Fe3+ used in the conventional method in the mechanism of forming barium ferrite. Indeed the efficiency of the synthesis and the quality of the product and the lack of impurities such as Fe2O3 and BaFe2O4 were improved when Fe2+ was included. However, the amount of ferrous ions that could be included to obtain the desired product was limited with an optimum ratio of 2:8 for FeCl2/FeCl3 when only 2h of reaction time were needed. It was also found that the role of trivalent Fe3+ could be successfully replaced by Al3+. Up to 50% of their on could be replaced by Al3+ in the reactants to produce Al- doped products. It was also found that the ratio of Fe2+/M3+ could be increased in the presence of Al3+ to produce high quality barium ferrite.

Influence of sodium chloride on seed germination and seedling root growth of cotton (Gossypium hirsutum L.)

Response of cotton (Gossypium hirsutum L. cv. NIAB-78) to salinity, in terms of seed germination, seedling root growth and root Na+ and K+ content was determined in a laboratory experiment. Cotton seeds were exposed to increasing salinity levels using germination water with Sodium chloride concentrations of 0, 50, 100, 150 and 200 mM, to provide different degrees of salt stress. Germinated seeds were counted and roots were harvested at 24, 48, 72 and 96 h after the start of the experiment. It appeared that seed germination was only slightly affected by an increase in salinity (in most cases the differences between treatment were non-significant), whereas root length, root growth rate, root fresh and dry weights were severely affected, generally highly significant differences in these variables were found for comparisons involving most combinations of salinity levels, in particular with increased incubation period. K+ contents decreased with increasing salinity levels, although differences in K+ content were only significant when comparing the control and the 4 salinity levels. Na+ content of the roots increased with increasing levels of NaCl in the germination water, suggesting an exchange of K+ for Na+. The ratio K+/Na+ strongly decreased with rising levels of salinity from around 4.5 for the control to similar to 1 at 200 mM NaCl.

Vibrational intensities VIII: CH3- and CD3- chloride, bromide and iodide

Absolute intensity measurements have been made on the fundamental vibrations of methyl chloride, bromide, and iodide, and their fully deuterated derivatives, by integrating the optical density over the absorption bands. The bands were fully pressure broadened by using up to 80 atmos of foreign gas. Band separations were made graphically. The results are analyzed in terms of the dipole moment derivatives with respect to symmetry coordinates in the molecule, (∂p/∂Si). The data on the different isotopic species are shown to yield consistent results, and this requirement of consistency has also been used as an aid in the analysis. In the E‐class vibrations the signs of the dipole moment derivatives have been determined unambiguously by assuming the permanent dipole to be directed CH3+☒X—.

The fundamental vibration-rotation band of hydrogen chloride

The fundamental vibration-rotational absorption band of hydrogen chloride near 3 45,t has been remeasured using higher resolving power than previously. The wave-lengths of the absorption lines have been determined more precisely, and the isotopic splitting of lines has been completely resolved. The results have provided new and more satisfactory values for the rotational constants Bi, and the centrifugal stretching constants Di, and their relative values for the two isotopic species agree closely with what is to be expected for the difference in mass. The positions of the lines in the pure rotational absorption spectrum have been calculated from the derived data, and agree closely with those recently observed. The bond lengths re for each isotopic species H35C1 and H37C1 is found to be 1-2744A.

Synthesis and characterization of carbamoyl methyl pyrazole(CMPz) compounds of palladium(II) chloride: the crystal and molecular structure of [PdCl2{(C3H3N2CH2CONBu2)-Bu-i}(2)]

Carbamoyl methyl pyrazole compound of palladium(II) chloride of the type [PdCl2L2] (where L = C5H7N2CH2CON(C4H9)(2), C5H7N2CH2CON((C4H9)-C-i)(2), C3H3N2CH2CON(C4H9)(2), or C3H3N2CH2CON((C4H9)-C-i)(2)) has been synthesized and characterized by IR and H-1 NMR spectroscopy. The structure of the compound [PdCl2{(C3H3N2CH2CONBu2}2)-Bu-i] has been determined by single crystal X-ray diffraction and shows that the ligands are bonded through the soft pyrazolyl nitrogen atom to the palladium(II) chloride in a trans disposition. (c) 2007 Elsevier B.V. All rights reserved.

Effects of calcium chloride and sodium hexametaphosphate on certain chemical and physical properties of soymilk

Soymilks with sodium hexametaphosphate (SHMP) (0% to 1.2%) and calcium chloride (12.50, 18.75, and 25.00 mM Ca),were analyzed for total Ca, Ca ion concentration, pH, kinematic viscosity, particle diameter, and sediment after pasteurization. Higher added Ca led to significant (P <= 0.05) increases in Ca ion concentration and significant (P <= 0.05) decreases in pH. At certain levels of SHMP, higher concentrations of added Ca significantly increased (P <= 0.05) kinematic viscosity, particle diameter, and sediment. Increasing SHMP concentration reduced Ca ion concentration, particle diameter, and dry sediment content, but reduced kinematic viscosity of samples (P <= 0.05). Adding SHMP up to 0.7% influenced pH of soymilk in different ways, depending on the level of Ca addition. When the pH of Ca-fortified soymilk was adjusted to a higher level, ionic Ca decreased as pH increased. Ihere was a negative linear relationship between the logarithm of ionic Ca concentration and the adjusted pH of the soymilk. Ionic Ca appeared to be a good indicator of thermally induced sediment formation, with little sediment being produced if ionic Ca was maintained below 0.4 mM.

Mucoadhesive interactions of amphiphilic cationic copolymers based on [2-(methacryloyloxy)ethyl]trimethylammonium chloride

Three series of water-soluble cationic copolymers have been synthesised by free-radical copolymerisation of [2-(methacryloyloxy)ethyl]-trimethylammonium chloride (MADQUAT) with methyl acrylate (MA), butyl acrylate (BA) and butyl methacrylate (BMA). The interactions between these copolymers and porcine stomach mucin have been studied in aqueous solutions using dynamic light scattering, zeta-potential measurements, turbidimetric titration and transmission electron microscopy (TEM). It was demonstrated that mixing aqueous dispersions of mucin with solutions of the cationic copolymers results in significant changes in size distribution and zeta-potential of its particles. It was found that an increase in the content of hydrophobic groups in copolymers leads to more efficient adsorption of macromolecules on the surface of mucin particles, which evidences the importance of hydrophobic effects in mucoadhesion. The efficiency of mucoadhesive interactions was found to be significantly dependent on pH, which affects the surface charge and aggregation stability of mucin. (C) 2007 Elsevier B.V. All rights reserved.

Comparative study of Barium Fluoride thin films produced by ion-beam sputtering and thermal evaporation

Coatings and filters for spaceflight far-infrared components require a robust, non-absorptive low-index thin film material to contrast with the typically higher refractive index infrared materials. Barium fluoride is one such material for the 10 to 20µm wavelength infrared region, however its optical and mechanical properties vary depending on the process used to deposit it in thin film form. Thin films of dielectric produced by thermal evaporation are well documented as having a lower packing density and refractive index than bulk material. The porous and columnar micro structure of these films causes possible deterioration of their performance in varied environmental conditions, primarily because of the moisture absorption. Dielectric thin films produced by the more novel technique of ion-beam sputtering are denser with no columnar micro structure and have a packing density and refractive index similar to the bulk material. A comparative study of Barium Fluoride (BaF2) thin films made by conventional thermal evaporation and ion-beam sputtering is reported. Films of similar thicknesses are deposited on Cadmium Telluride and Germanium substrates. The optical and mechanical properties of these films are then examined. The refractive index n of the films is obtained from applying the modified Manifacier's evvelope method to the spectral measurements made on a Perkin Elmer 580 spectrophotometer. An estimate is also made of the value of the extinction coefficient k in the infrared wavelength transparent region of the thin film. In order to study the mechanical properties of the BaF2 films, and evaluate their usefulness in spaceflight infrared filters and coatings, the thin film samples are subjected to MIL-F-48616 environmental tests. Comparisons are made of their performance under these tests.

Molecular dynamics simulations of threadlike cetyltrimethylammonium chloride micelles: effects of sodium chloride and sodium salicylate salts

We use atomistic molecular dynamics simulations to probe the effects of added sodium chloride (NaCl) and sodium salicylate (NaSal) salts on the spherical-to-threadlike micelle shape transition in aqueous solutions of cetyltrimethylammonium chloride (CTAC) surfactants. Long threadlike micelles are found to be unstable and break into spherical micelles at low concentrations or NaCl, but remain stable for 20 ns above a threshold value of [NaCl] approximate to 3.0 M, which is about 2.5 times larger than the experimental salt concentration at which the transition between spherical and rodlike micelles occurs. The chloride counterions associate weakly oil the surface of the CTAC micelles with the degree of counterion dissociation decreasing slightly with increasing [NaCl] on spherical micelles, but dropping significantly on the threadlike micelles tit high [NaCl]. This effect indicates that the electrolyte ions drive the micellar shape transition by screening the electrostatic repulsions between the micellar headgroups, The aromatic salicylate counterions, on the other hand, penetrate inside the micelle with their hydrophilic groups staying in the surfactant headgroup region and the hydrophobic groups partially embedded into the hydrophobic core of the micelle. The strong association of the salicylate ions with the surfactant headgroups leads to dense packing of the surfactant molecules, which effectively reduces the surface area per surfactant, and increases intramicellar ordering of the surfactant headgroups, favoring the formation of long threadlike micelles. Simulation predictions of the geometric and electrostatic properties of the spherical and threadlike micelles are in good agreement with experiments.

Coordination behavior of pyridylmethylthioether system with cupric chloride and cupric bromide: CS bond cleavage and crystal structures

The coordination behavior of pyridylmethylthioether type of organic moieties having N2S2 donor set [L-1=1,2-bis(2-pyridylmethylthio)ethane, L-2 = 1,3-bis(2-pyridylmethyl-thio)propane and L-3 = 1,4-bis(2-pyridylmethylthio)butane] with copper(II) chloride and copper(II) bromide have been studied in different chemical environments. Copper(II) chloride assisted C-S bond cleavage of the organic moieties leading to the formation of copper(II) picolinate derivatives, whereas, under similar experimental conditions, no C-S bond cleavage was observed in the reaction with copper(II) bromide. The resulted copper(II) complexes isolated from the different mediums have been characterized by spectroscopic and X-ray crystallographic tools.

Preparation and magnetic properties of La–Mn and La–Co doped barium hexaferrites prepared via an improved co-precipitation/molten salt method

LaMn and LaCo doped barium hexaferrites of formula Ba(1-x)LaxFe(12-x)MxO19 (M=Mn, Co) (x=0.05 to 0.40) were prepared with an improved co-precipitation/molten salt method. For the synthesis, aqueous solutions of the appropriate metal chlorides were prepared in the ratio required except that the initial mole ratio of Fe and dopants to Ba was chosen to be 11:1, and then mixed with excess Na2CO3. The solutions were then cooled, filtered off, dried, then mixed with KCl flux, and heated at 450 degrees C and for 2 h. The temperature was then raised to 950 degrees C and kept for 4 h, then cooled. This new synthesis method, which employs a lower temperature and shorter reaction time, gives products with improved crystallinity and purity while the saturation magnetization and coercivity values are comparable with those synthesized via the high temperature method.

Optimizing the methods of synthesis for barium hexagonal ferrite: an experimental and theoretical study

M-type barium hexaferrite (BaM) is a hard ferrite, crystallizing in space group P6(3)/mmc possessing a hexagonal magneto-plumbite structure, which consists of alternate hexagonal and spinel blocks. The structure of BaM is thus related to those of garnet and spinel ferrite. However the material has proved difficult to synthesize. By taking into account the presence of the spinel block in barium hexagonal ferrite, highly efficient new synthetic methods were devised with routes significantly different from existing ones. These successful variations in synthetic methods have been derived by taking into account a detailed investigation of the structural features of barium hexagonal ferrite and the least change principle whereby configuration changes are kept to a minimum. Thus considering the relevant mechanisms has helped to improve the synthesis efficiencies for both hydrothermal and co-precipitation methods by choosing conditions that invoke the formation of the cubic block or the less stable Fe3O4. The role played by BaFe2O4 in the synthesis is also discussed. The distribution of iron from reactants or intermediates among different sites was also successfully explained. The proposed mechanisms are based on the principle that the cubic block must be self-assembled to form the final product. Thus, it is believed that these formulated mechanisms should be helpful in designing experiments to obtain a deeper understanding of the synthesis process and to investigate the substitution of magnetic ions with doping ions.

Preparation and magnetic properties of barium ferrites substituted with manganese, cobalt, and tin

Barium ferrites substituted by Mn–Sn, Co–Sn, and Mn–Co–Sn with general formulae BaFe12−2xMnxSnxO19 (x=0.2–1.0), BaFe12−2xCoxSnxO19 (x=0.2–0.8), and BaFe12−2xCox/2Mnx/2SnxO19 (x=0.1–0.6), respectively, have been prepared by a previously reported co-precipitation method. The efficiency of the method was refined by lowering the reaction temperature and shortening the required reaction time, due to which crystallinity improved and the value of saturated magnetization increased as well. Low coercivity temperature coefficients, which are adjustable by doping, were achieved by Mn–Sn and Mn–Co–Sn doping. Synthesis efficiency and the effect of doping are discussed taking into account accumulated data concerning the synthesis and crystal structure of ferrites.