High Permittivity and Low Ceramics in the Bao-SrO-Nb2O5 System

A new group of compounds with composition (Ba5-xSrx) Nb4015, having high permittivity and low loss have been prepared and characterized in the microwave frequency region . X-ray diffraction studies showed that monophase compound existed for all values of x from 0 to 5. Microwave dielectric properties such as and c f showed smooth variation with x , while the unloaded quality factor (Qu) showed remarkable improvement with x

New High Permittivity and Low Loss Ceramics in the Bao-Ti02- Nb205 Composition

New dielectric ceramics with formula BaTi3Nb4, O„ and Ba6Til4Nbz039 have been prepared and characterized. BaTi3Nba017 was densified to 92% of TD after firing at 1310 oC for 4 h. However, Ba6Ti 1 4Nb2O39 fired under optimized conditions (1260 ` C for 4 h) showed only 85% TD together with secondary phase. The crystal system of both of the compositions is orthorhombic

Preparation, Characterization and Dilectric Properties of Ceramics in the BaO-Nd2O3-TiO2 System

The dielectric ceramics BaNd2Ti3Oto, BaNd2Ti4O12 and BaNd2Ti5O14 have been prepared by Conventional solid state ceramic route. The sintered ceramic samples have been characterized by X-ray diffraction and Scanning Electron Microscopy (SEM). The dielectric properties in the microwave frequency range have been measured using conventional microwave dielectric resonator methods. The BaNd2Ti1O10, BaN2Ti4O12 and BaNd2Ti5O14 have dielectric constants (Er) ~ 60, 84 and 77 respectively. They have relatively high quality factors

Microwave Dielectric Properties of BaO -2CeO2-nTiO2 Ceramics

The BaO-2CeO2-nTiO2 ceramics with n = 3, 4 and 5 have been prepared with CeO2 as starting material . The ceramics have been characterized using scanning electron microscopy , X-ray diffraction , Raman and X-ray photoelectron spectroscopy techniques. The microwave dielectric properties have been measured using standard dielectric resonator techniques . BaO-2CeO2-3TiO2 (123), BaO-2CeO2-4TiO2 ( 124) and BaO-2CeO2-5TiO2 ( 125) ceramics showed dielectric constants of 38, 27 and 32, respectively . All the ceramics showed fairly good unloaded Q - factors . 124 and 125 compounds exhibited low tf values, while 123 showed a high rf value