Chemical and Morphological Features of Dental Composite Resin: Influence of Light Curing Units and Immersion Media

Aims: The study evaluated the influence of light curing units and immersion media on superficial morphology and chemistry of the nanofilled composite resin Supreme XT (3M) through the EDX analysis and SEM evaluation. Light curing units with different power densities and mode of application used were XL 3000 (480 mW/cm(2)), Jet Lite 4000 Plus (1230mW/cm(2)), and Ultralume Led 5 (790 mW/cm(2)) and immersion media were artificial saliva, Coke(R), tea and coffee, totaling 12 experimental groups. Specimens (10 mm X 2 mm) were immersed in each respective Solution for 5 min, three times a day, during 60 days and stored in artificial saliva at 37 degrees C +/- 1 degrees C between immersion periods. Topography and chemical analysis was qualitative. Findings: Groups immersed in artificial saliva, showed homogeneous degradation of matrix and deposition of calcium at the material surface. Regarding coffee, there was a reasonable chemical degradation with loss of load particles and deposition of ions. For tea, superficial degradation occurred in specific areas with deposition of calcium, carbon. potassium and phosphorus. For Coke(R), excessive matrix degradation and loss of load particles with deposition of calcium, sodium, and potassium. Conclusion: Light curing units did not influence the superficial morphology of composite resin tested, but the immersion beverages did. Coke(R) affected material`s surface more than did the other tested drinks. Microsc. Res. Tech. 73:176-181, 2010. (c) 2009 Wiley-Liss Inc.

Influence of NaHCO(3) Powder on Translucency of Microfilled Composite Resin Immersed in Different Mouthrinses

The regular use of mouthrinses, particularly when combined with the use of air-powder polishing, could affect the appearance of tooth-colored restorations. The current study sought to evaluate the effect of NaHCO(3) powder on translucency of a microfilled composite resin immersed in different mouthrinses, at distinct evaluation periods. Eighty disk-shaped specimens of composite resin (Durafill VS, Heraeus Kulzer GmbH & Co. KG, Hanau, Germany) were prepared. The composite specimens were then randomly allocated into two groups according to the surface treatment: exposure to NaHCO(3) powder (10 seconds) or nonexposure, and they were randomly assigned into four subgroups, according to the mouthrinses employed (N = 10): Periogard (Colgate/Palmolive, Sao Bernardo do Campo, SP, Brazil), Cepacol (Aventis Pharma, Sao Paulo, SP, Brazil), Plax (Colgate/Palmolive), and distilled water (control group). The samples were immersed for 2 minutes daily, 5 days per week, over a 4-month test period. Translucency was measured with a transmission densitometer at seven evaluation periods. Statistical analyses (analysis of variance and Tukey`s test) revealed that: distilled water presented higher translucency values (86.72%); Periogard demonstrated the lowest translucency values (72.70%); and Plax (74.05%) and Cepacol (73.32%) showed intermediate translucency values, which were statistically similar between them (p > 0.01). NaHCO(3) air-powder polishing increased the changes in translucency associated with the mouthrinses. Air-powder polishing alone had no effect on material translucency. Translucency percent was gradually decreased from 1 week of immersion up to 4 months. It may be concluded that the NaHCO(3) powder and the tested mouthrinses have affected the translucency of microfilled composite resin, according to the tested time. CLINICAL SIGNIFICANCE During the last decade, the demand for composite resin restorations has grown considerably, however, controversy persists regarding the effect of surface roughness on color stability.

Measurement of shrinkage of composite resin by laser speckle contrast analysis

The aim of this study was to evaluate the shrinkage of a microhybrid dental composite resin photo-activated by one LED with different power densities by means of speckle technique. The dental composite resin Filtek (TM) Z-250 (3M/ESPE) at color A(2) was used for the samples preparation. Uncured composite was packed in a metallic mold and irradiated during 20 s from 100 to 1000 mW cm(-2). For the photo-activation of the samples, it was used a LED prototype (Light Emission Diode) with wavelength centered at 470 nm and adjustable power density until 1 W cm(-2). The speckle patterns obtained from the bottom composite surfaces were monitored using a CCD camera without lens. The speckle field is recorded in a digital picture and stored by CCD camera as the carrier of information on the displacement of the tested surface. The calculated values were obtained for each pair of adjacent patterns and the changes in speckle contrast as a function of time were obtained from six repeated measurements. The speckle contrasts obtained from the bottom surface with 100 mW cm(-1) were smaller than those than the other power densities. The higher power densities provided the higher shrinkage.

Influence of Er:YAG laser on surface treatment of aged composite resin to repair restoration

The purpose of this study was to investigate the effect of Er:YAG laser on surface treatment to the bond strength of repaired composite resin after aged. Sixty specimens (n = 10) were made with composite resin (Z250, 3M) and thermocycled with 500 cycles, oscillating between 5 to 55A degrees C. The specimens were randomly separated in six groups which suffered the following superficial treatments: no treatment (GI, control), wearing with diamond bur (GII), sandblasted with aluminum oxide with 27.5 A mu m particles (GIII) for 10 s, 200 mJ Er:YAG laser (GIV), 300 mJ Er:YAG laser (GV), and 400 mJ Er:YAG laser (GVI), with the last 3 groups under a 10 Hz frequency for 10 s. Restoration repair was done using the same composite. The shear test was done into the Universal testing machine MTS-810. Analyzing the results through ANOVA and Tukey test, no significant differences were found (p-value is 0.5120). Average values analysis showed that superficial treatment with aluminum oxide presented the highest resistance to shear repair interface (8.91MPa) while 400 mJ Er:YAG laser presented the lowest (6.76 MPa). Fracture types analysis revealed that 90% suffered cohesive fractures to GIII. The Er:YAG laser used as superficial treatment of the aged composite resin before the repair showed similar results when used diamond bur and sandblasting with aluminum oxide particles.

Influence of pre-heat treatment and different light-curing units on Vickers hardness of a microhybrid composite resin

The aim of this study was to evaluate the hardness of a dental composite resin submitted to temperature changes before photo-activation with two light-curing unite (LCUs). Five samples (4 mm in diameter and 2 mm in thickness) for each group were made with pre-cure temperatures of 37, 54, and 60A degrees C. The samples were photo-activated with a conventional quartz-tungsten-halogen (QTH) and blue LED LCUs during 40 s. The hardness Vickers test (VHN) was performed on the top and bottom surfaces of the samples. According to the interaction between light-curing unit and different pre-heating temperatures of composite resin, only the light-curing unit provided influences on the mean values of initial Vickers hardness. The light-curing unit based on blue LED showed hardness mean values more homogeneous between the top and bottom surfaces. The hardness mean values were not statistically significant difference for the pre-cure temperature used. According to these results, the pre-heating of the composite resin provide no influence on Vickers hardness mean values, however the blue LED showed a cure more homogeneous than QTH LCU.

Degree of Conversion and Temperature Increase of a Composite Resin Light Cured with an Argon Laser and Blue LED

Different light sources and power densities used on the photoactivation process may provide changes in the degree of conversion (DC%) and temperature ( T) of the composite resins. Thus, the purpose of this study was to evaluate the DC (%) and T (degrees C) of the microhybrid composite resin (Filtek (TM) Z-250, 3M/ESPE) photoactivated with one argon laser and one LED (light-emitting diode) with different power densities. For the KBr pellet technique, the composite resin was placed into a metallic mould (2-mm thickness, 4-mm diameter) and photoactivated as follows: a continuous argon laser (CW) and LED LCUs with power density values of 100, 400, 700, and 1000 mW/cm(2) for 20 s. The measurements for DC (%) were made in a FTIR spectrometer Bomen ( model MB 102, Quebec, Canada). Spectroscopy ( FTIR) spectra for both uncured and cured samples were analyzed using an accessory of the reflectance diffusion. The measurements were recorded in absorbance operating under the following conditions: 32 scans, 4 cm(-1) resolution, 300 to 4000-cm(-1) wavelength. The percentage of unreacted carbon double bonds (% C=C) was determined from the ratio of absorbance intensities of aliphatic C=C (peak at 1638 cm(-1)) against an internal standard before and after the curing of the specimen: aromatic C-C (peak at 1608 cm(-1)). For T (degrees C), the samples were created in a metallic mould (2-mm thickness, 4-mm diameter) and photoactivated for 20 s. The thermocouple was attached to the multimeter allowing temperature readings. The DC (%) and T (degrees C) were submitted to ANOVA and Tukey`s test (p < 0.05). The degree of conversion values varied from 35.0 to 50.0% ( 100 to 1000 mW/cm(2)) for an argon laser and from 41.0 to 49% (100 to 1000 mW/cm(2)) for an LED. The temperature change values varied from 1.1 to 13.1 degrees C (100 to 1000 mW/cm(2)) for an argon laser and from 1.9 to 15.0 degrees C (100 to 1000 mW/cm(2)) for an LED. The power densities showed a significant effect on the degree of conversion and changes the temperature for both light-curing units.

Effect of power densities and irradiation times on the degree of conversion and temperature increase of a microhybrid dental composite resin

The different parameters used for the photoactivation process provide changes in the degree of conversion (DC%) and temperature rise (TR) of the composite resins. Thus, the purpose of this study was to evaluate the DC (%) and TR of the microhybrid composite resin photoactivated by a new generation LED. For the KBr pellet technique, the composite resin was placed into a metallic mould (1-mm thickness and 4-mm diameter) and photoactivated as follows: continuous LED LCU with different power density values (50-1000 mW/cm(2)). The measurements for the DC (%) were made in a FTIR Spectrometer Bomen (model MB-102, Quebec-Canada). The spectroscopy (FTIR) spectra for both uncured and cured samples were analyzed using an accessory for the diffuse reflectance. The measurements were recorded in the absorbance operating under the following conditions: 32 scans, 4-cm(-1) resolution, and a 300 to 4000-cm(-1) wavelength. The percentage of unreacted carbon-carbon double bonds (% C=C) was determined from the ratio of the absorbance intensities of aliphatic C=C (peak at 1638 cm(-1)) against an internal standard before and after the curing of the specimen: aromatic C-C (peak at 1608 cm-1). For the TR, the samples were made in a metallic mould (2-mm thickness and 4-mm diameter) and photoactivated during 5, 10, and 20 s. The thermocouple was attached to the multimeter to allow the temperature readings. The DC (%) and TR were calculated by the standard technique and submitted to ANOVA and Tukey`s test (p < 0.05). The degree of conversion values varied from 35.0 (+/- 1.3) to 45.0 (+/- 2.4) for 5 s, 45.0 (+/- 1.3) to 55.0 (+/- 2.4) for 10 s, and 47.0 (+/- 1.3) to 52.0 (+/- 2.4) for 20 s. For the TR, the values ranged from 0.3 (+/- 0.01) to 5.4 (+/- 0.11)degrees C for 5 s, from 0.5 (+/- 0.02) to 9.3 (+/- 0.28)degrees C for 10 s, and from 1.0 (+/- 0.06) to 15.0 (+/- 0.95)degrees C for 20 s. The power densities and irradiation times showed a significant effect on the degree of conversion and temperature rise.

Changes in the temperature of a dental light-cured composite resin by different light-curing units

The purpose of this study was to evaluate the temperature increase during the polymerization process through the use of three different light-curing units with different irradiation times. One argon laser (Innova, Coherent), one halogen (Optilight 501, Demetron), and one blue LED (LEC 1000, MM Optics) LCU with 500 mW/cm(2) during 5, 10, 20, 30, 40, 50, and 60 s of irradiation times were used in this study. The composite resin used was a microhybrid Filtek Z-250 (3M/ESPE) at color A(2). The samples were made in a metallic mold 2 mm in thickness and 4 mm in diameter and previously light-cured during 40 s. A thermocouple (Model 120-202 EAJ, Fenwal Electronic, Milford, MA, USA) was introduced in the composite resin to measure the temperature increase during the curing process. The highest temperature increase was recorded with a Curing Light 2500 halogen LCU (5 and 31 degrees C after 5 and 60 s, respectively), while the lowest temperature increase was recorded for the Innova LCU based on an argon laser (2 and 11 degrees C after 5 and 60 s, respectively). The temperature recorded for LCU based on a blue LED was 3 and 22 degrees C after 5 and 60 s, respectively. There was a quantifiable amount of heat generated during the visible light curing of a composite resin. The amount of heat generated was influenced by the characteristics of the light-curing units used and the irradiation times.

Influence of water flow rate on shear bond strength of resin composite to Er : YAG cavity preparation

Purpose: To evaluate in vitro the influence of water flow rate on shear bond strength of a resin composite to enamel and dentin after Er:YAG cavity preparation. Methods: Ten bovine incisors were selected and roots removed. Crowns were sectioned in four pieces, resulting in 40 samples that were individually embedded in polyester resin (n=10), and ground to plane the enamel and expose the dentin. The bonding site was delimited and samples were randomly assigned according to cavity preparation: (1) Er:YAG/1.0 mL/minute; (2) Er:YAG/1.5 mL/minute; (3) Er:YAG/2.0 mL/minute and (4) High speed handpiece/bur (control group). Samples were fixed to a metallic device, where composite resin cylinders were prepared. Subsequently, they were stored for 24 hours and subjected to a shear bond strength test (500N at 0.5 mm/minute). Results: Means (MPa) were: enamel: 1: 12.8; 2: 16.8; 3: 17.5; 4: 36.0 and Dentin: 1: 13.6; 2: 18.7; 3: 12.1; 4: 21.3. Data were submitted to ANOVA and Tukey`s test. Adhesion to enamel was more efficient than for dentin. The cavities prepared with conventional bur (control) presented higher statistically significant bond strength values (P<0.05) than for Er:YAG laser for both enamel and dentin. No significant differences were observed between water flow rates employed during enamel ablation. For dentin, the shear bond strength of 2.0 mL/minute water flow rate was lower than for 1.5 mL/minute and 1.0 mL/minute rates. The Er:YAG laser adversely affected shear bond strength of resin composite to both enamel and dentin, regardless of the water flow rate used.

Effect of Pre-Heating Resin Composite and Light-Curing Units on Monomer Conversion

The purpose of this study was to evaluate the effect of pre-heating resin composite photo-cured with light-curing units (LCU) by FT-IR. Twenty specimens were made in a metallic mold (4 mm diameter x 2 mm thick) from composite resin-Tetric Ceram (R) (Ivoclar/Vivadent) at room temperature (25 degrees C) and pre heated to 37, 54, and 60 degrees C. The specimens were cured with halogen curing light (QTH) and light emitted by diodes (LED) during 40 s. Then, the specimens were pulverized, pressed with KBr and analyzed with FT-IR. The data were submitted to statistical analysis of variance and Kruskal-Wallis test. Study data showed no statistically significant difference to the degree of conversion for the different light curing units (QTH and LED) (p > 0.05). With the increase of temperature there was significant increase in the degree of conversion (p < 0.05). In this study were not found evidence that the light curing unit and temperature influenced the degree of conversion.

Effect of different dental composite resins on the polymerization process

Dental composite resins possess good esthetic properties, and are currently among the most popular dental restorative materials. Both organic and inorganic phases might influence the material behavior, the filler particle features and rate are the most important factors related to improvement of the mechanical properties of resin composites. Thus, the objective of this study was to evaluate the effect of three different composite resins on the polymerization process by Vickers hardness test. The samples were prepared using three different composite resins, as follow: group I-P-60 (3M/ESPE); group II-Herculite XRV (Kerr), and group III-Durafill (Heraeus-Kulzer). The samples were made in a polytetrafluoroethylene mould, with a rectangular cavity measuring 7 mm in length, 4 mm in width, and 3 mm in thickness. The samples were photo-activated by one light-curing unit based on blue LEDs (Ultrablue III-DMC/Brazil) for 20 and 40 s of irradiation times. The Vickers hardness test was performed 24 h after the photo-activation until the standardized depth of 3 mm. The Vickers hardness mean values varied from 158.9 (+/- 0.81) to 81.4 (+/- 1.94) for P-60, from 138.7 (+/- 0.37) to 61.7 (+/- 0.24) for Herculite XRV, and from 107. 5 (+/- 0.81) to 44.5 (+/- 1.36) for Durafill composite resins photo-activated during 20 s for the 1st and 2nd mm, respectively. During 40 s of photo-activation, the Vickers hardness mean values were: from 181.0 (+/- 0.70) to 15.6 (+/- 0.29) for P-60, and from 161.8 (+/- 0.41) to 11.2 (+/- 0.17) for Herculite XRV composite resins, for the 1st and 3th mm, respectively. For Durafill composite resin the mean values varied from 120.1 (+/- 0.66) to 61.7 (+/- 0.20), for the 1st and 2nd mm, respectively. The variation coefficient (CV) was in the most of the groups lower than 1%, then the descriptive statistic analysis was used. The Vickers hardness mean values for Durafill were lower than P-60 and Herculite XRV composite resins for 20 and 40 s of irradiation time. The polymerization process was greatly affected by the composition of the composite resins.

Effect of Two Restorative Materials on Root Dentine Erosion

This study sought to evaluate the microhardness of root dentine adjacent to glass-ionomer and composite resin restorations after erosive challenge. A crossover study was performed in two phases of 4 consecutive days each. One hundred twelve bovine root dentine slabs were obtained, and standardized box-shaped cavities were prepared at center of each specimen. The prepared cavities were randomly restored with glass-ionomer cement or composite resin. The slabs were randomly assigned among 14 volunteers, which wore intraoral palatal device containing four restored root dentin slabs. Starting on the second day, half of the palatal acrylic devices were immersed extraorally in a lemonade-like carbonated soft drink for 90 s, four times daily for 3 days. Alter 3-day wash-out, dentine slabs restored with the alternative material were placed into palatal appliance and the volunteers started the second phase of this study. After erosive challenges. microhardness measurements were performed. Regardless of the restorative material employed, eroded specimens demonstrated lower microhardness value (p < 0.0001). At eroded condition examined in this study, dentine restored with glass-ionomer cement showed higher microhardness values (p < 0.0001). It may be concluded that the glass-ionomer cement decreases the progression of root dentine erosion at restoration margin. (C) 2010 Wiley Periodicals, Inc J Biomed Mater Res Part B Appl Biomater 93B 304-305, 2010

Thermal analysis and structural investigation of different dental composite resins

The structural and thermal properties of three different dental composite resins, Filtek (TM) Supreme XT, Filtek (TM) Z-250 and TPHA (R)(3) were investigated in this study. The internal structures of uncured and cured resins with blue light-emitting diodes (LEDs) were examined by Micro-Raman spectroscopy. Thermal analysis techniques as DSC, TG and DTG methods were used to investigate the temperature characteristics, as glass transition (T (g) ), degradation, and the thermal stability of the resins. The results showed that the TPHA (R)(3) and Filtek (TM) Supreme XT presented very similar T (g) values, 48 and 50A degrees C, respectively, while the Filtek (TM) Z-250 composite resin presented a higher one, 58A degrees C. AFM microscope was utilized in order to analyze the sample morphologies, which possess different fillers. The composed resin Filtek (TM) Z-250 has a well interconnected more homogeneous morphology, suggesting a better degree of conversion correlated to the glass phase transition temperature. The modes of vibration of interest in the resin were investigated using Raman spectroscopy. It was possible to observe the bands representative for the C=C (1630 cm(-1)) and C=O(1700 cm(-1)) vibrations were studied with respect to their compositions and polymerization. It was observed that the Filtek (TM) Z -250 resin presents the best result related to the thermal properties and polymerization after light curing among the other resins.

Continuous and gradual photo-activation methods: influence on degree of conversion and crosslink density of composite resins

Thermal properties and degree of conversion (DC%) of two composite resins (microhybrid and nanocomposite) and two photo-activation methods (continuous and gradual) displayed by the light-emitting diode (LED) light-curing units (LCUs) were investigated in this study. Differential scanning calorimetry (DSC) thermal analysis technique was used to investigate the glass transition temperature (T(g)) and degradation temperature. The DC% was determined by Fourier transform infrared spectroscopy (FT-IR). The results showed that the microhybrid composite resin presented the highest T(g) and degradation temperature values, i.e., the best thermal stability. Gradual photo-activation methods showed higher or similar T(g) and degradation temperature values when compared to continuous method. The Elipar Freelight 2 (TM) LCU showed the lowest T(g) values. With respect to the DC%, the photo-activation method did not influence the final conversion of composite resins. However, Elipar Freelight 2 (TM) LCU and microhybrid resin showed the lowest DC% values. Thus, the presented results suggest that gradual method photo-activation with LED LCUs provides adequate degree of conversion without promoting changes in the polymer chain of composite resins. However, the thermal properties and final conversion of composite resins can be influenced by the kind of composite resin and LCU.

Influence of light guide tip used in the photo-activation on degree of conversion and hardness of one nanofilled dental composite

The aim of this study was to evaluate the degree of conversion and hardness of a dental composite resin Filtek (TM) Z-350 (3M ESPE, Dental Products St. Paul, MN) photo-activated for 20 s of irradiation time with two different light guide tips, metal and polymer, coupled on blue LED Ultraled LCU (Dabi Atlante, SP, Brazil). With the metal light tip, power density was of 352 and with the polymer was of 456 mW/cm(2), respectively. Five samples (4 mm in diameter and 2mm in thickness-ISO 4049), were made for each Group evaluated. The measurements for DC (%) were made in a Nexus-470 FT-IR, Thermo Nicolet, E.U.A. Spectroscopy (FTIR). Spectra for both uncured and cured samples were analyzed using an accessory of reflectance diffuse. The measurements were recorded in absorbance operating under the following conditions: 32 scans, 4 cm(-1) resolution, 300-4000 cm(-1) wavelength. The percentage of unreacted carbon double bonds (% C=C) was determined from the ratio of absorbance intensities of aliphatic C=C (peak at 1637 cm(-1)) against internal standard before and after curing of the sample: aromatic C-C (peak at 1610 cm(-1)). The Vickers hardness measurements (top and bottom surfaces) were performed in a universal testing machine (Buehler MMT-3 digital microhardness tester Lake Bluff, Illinois USA). A 50 gf load was used and the indenter with a dwell time of 30 s. The data were submitted to the test t Student at significance level of 5%. The mean values of degree of conversion for the polymer and metal light guide tip no were statistically different (p = 0.8389). The hardness mean values were no statistically significant different among the light guide tips (p = 0.6244), however, there was difference between top and bottom surfaces (p < 0.001). The results show that so much the polymer light tip as the metal light tip can be used for the photo-activation, probably for the low quality of the light guide tip metal.