Insight into the key aspects of the regeneration process in the NOx storage reduction (NSR) reaction probed using fast transient kinetics coupled with isotopically labelled (NO)-N-15 over Pt and Rh-containing Ba/Al2O3 catalysts

For the first time, the coupling of fast transient kinetic switching and the use of an isotopically labelled reactant (15NO) has allowed detailed analysis of the evolution of all the products and reactants involved in the regeneration of a NOx storage reduction (NSR) material. Using realistic regeneration times (ca. 1 s) for Pt, Rh and Pt/Rh-containing Ba/Al2O3 catalysts we have revealed an unexpected double peak in the evolution of nitrogen. The first peak occurred immediately on switching from lean to rich conditions, while the second peak started at the point at which the gases switched from rich to lean. The first evolution of nitrogen occurs as a result of the fast reaction between H2 and/or CO and NO on reduced Rh and/or Pt sites. The second N2 peak which occurs upon removal of the rich phase can be explained by reaction of stored ammonia with stored NOx, gas phase NOx or O2. The ammonia can be formed either by hydrolysis of isocyanates or by direct reaction of NO and H2.

The study highlights the importance of the relative rates of regeneration and storage in determining the overall performance of the catalysts. The performance of the monometallic 1.1%Rh/Ba/Al2O3 catalyst at 250 and 350 °C was found to be dependent on the rate of NOx storage, since the rate of regeneration was sufficient to remove the NOx stored in the lean phase. In contrast, for the monometallic 1.6%Pt/Ba/Al2O3 catalyst at 250 °C, the rate of regeneration was the determining factor with the result that the amount of NOx stored on the catalyst deteriorated from cycle to cycle until the amount of NOx stored in the lean phase matched the NOx reduced in the rich phase. On the basis of the ratio of exposed metal surface atoms to total Ba content, the monometallic 1.6%Pt/Ba/Al2O3 catalyst outperformed the Rh-containing catalysts at 250 and 350 °C even when CO was used as a reductant.

The use of short time-on-stream in situ spectroscopic transient kinetic isotope techniques to investigate the mechanism of hydrocarbon selective catalytic reduction (HC-SCR) of NOx at low temperatures

The problem of differentiating between active and spectator species that have similar infrared spectra has been addressed by developing short time-on-stream in situ spectroscopic transient isotope experimental techniques (STOS-SSITKA). The techniques have been used to investigate the reaction mechanism for the reduction of nitrogen oxides (NOx) by hydrocarbons under lean-burn (excess oxygen) conditions on a silver catalyst. Although a nitrate-type species tracks the formation of isotopically labeled dinitrogen, the results show that this is misleading because a nitrate-type species has the same response to an isotopic switch even under conditions where no dinitrogen is produced. In the case of cyanide and isocyanate species, the results show that it is possible to differentiate between slowly reacting spectator isocyanate species, probably adsorbed on the oxide support, and reactive isocyanate species, possibly on or close to the active silver phase. The reactive isocyanate species responds to an isotope switch at a rate that matches that of the rate of formation of the main product, dinitrogen. It is concluded that these reactive isocyanates could potentially be involved in the reduction of NOx whereas there is no evidence to support the involvement of nitrate-type species that are observable by infrared spectroscopy.

Origin of double dinitrogen release feature during fast switching between lean and rich cycles for NOx storage reduction catalysts

The performance of NOx storage and reduction over 1.5 wt% Pt/20 wt% KNO3/K2Ti8O17 and 1.5 wt% Pt/K2Ti8O17 catalysts has been investigated using combined fast transient kinetic switching and isotopically labelled (NO)-N-15 at 350 degrees C. The evolution of product N-2 has revealed two significant peaks during 60 s lean/1.3 s rich switches. It also found that the presence of CO2 in the feed affects the release of N-2 in the second peak. Regardless of the presence/absence of water in the feed, only one peak of N-2 was observed in the absence of CO2. Gas-phase NH3 was not observed in any of the experiments. However, in the presence of CO2 the results obtained from in situ DRIFTS-MS analysis showed that isocyanate species are formed and stored during the rich cycles, probably from the reaction between NOx and CO, in which CO was formed via the reverse water-gas shift reaction. 

Mechanochemical preparation of Ag catalysts for the n-octane-SCR de-NOx reaction: Structural and reactivity effects

Mechanochemical preparation of Ag/Al2O3 catalysts used for the selective catalytic reduction of NOx using hydrocarbons has been shown to substantially increase the activity of the catalyst in comparison with Ag/Al2O3 prepared by wet impregnation. The effect of using different ball-milling experimental parameters on both the structure of the material as well as the catalyst activity has been investigated and the optimum conditions established. A phase transition from γ- to α-alumina was observed milling at high speeds which was found to result in lower catalyst activities. At lower milling speeds both fracturing and agglomeration of the alumina support can be observed depending on the grinding time. However, due to ball-milling, a general enhancement in the NOx reduction activity was observed for all catalysts compared with the conventionally prepared catalysts irrespective of the reductant used. Transient DRIFTS-MS experiments were performed to investigate the effect of H2 in the absence and presence of water on the SCR reaction over catalysts prepared by both ball milling and wet impregnation. In-situ DRIFTS-MS analysis revealed significant differences in both gas phase and surface species. Most notably, isocyanate species were formed significantly more quickly and at higher surface concentration in the case of the mechanochemically prepared catalyst.