Modificação superficial de fibras de juta com descarga corona para melhora da aderência com matriz poliéster

Seeking alternatives for the total or partial substitution of synthetic fibers for natural fibers, with reinforcement in polymeric materials, this work was conducted with the objective of evaluating the treatment with corona discharge on the adherence of juta fibers with resin. The fibers were exposed to corona discharge for 1, 5, 10 and 15 minutes, as well as after treatment with hot water, molding composites fiber-reinforced with filaments treated for 10 and 15 minutes, and without the treatment. The chemical structures were evaluated by spectrometry in the region of Fourier transform infrared with attenuated total reflection (FTIR/ATR), observing the formation of a new band and the increase in the absorption of groupings with oxygen. The thermal analyses, such as thermogravimetry (TG) and differential scanning calorimetry (DSC) revealed the degradation of cellulose, hemicellulose and lignin. The microstructural characterization by scanning electron microscopy (SEM) showed changes in the surface of the fiber, such as roughness, superficial depressions, surface degradation and cavity formation. The adhesion of the fibers was evaluated by the pullout test, allowing us to verify the increase in adhesion strength after treatment with corona discharge. In conclusion, the treatment with corona discharge changes the surface of the juta fibers, resulting in better adherence with the resin.

Estudos químicos e anatômicos de cascas de clones de Eucalyptus

The barks generated from the wood processing industries are wastes generated in significant quantities, becoming interesting to have basic studies of their anatomical and chemical properties in order to make better use of this material. This study aimed to carry out anatomical studies, chemical and tannins from the barks of commercial clones of Eucalyptus. For this, permanent histological slides for anatomical characterization and percentage of cellular elements were prepared; and cellular elements were dissociated for biometry of the elements. The analyses were related to chemical extractives, ash, lignin, suberin, sugars, phenols, tannins, flavonoids and antioxidant activity of the extracts. The tannins were extracted in pure water and with water mixed with sodium sulfite, and were subsequently evaluated the properties by FT-IR. It was verified by the anatomical characterization and chemical quantification, the similarity between the clones. Regarding the biometrics of cellular elements, statistically significant differences were not observed for the following parameters: length and diameter of sieve tube, axial parenchyma diameter, and rays hight. The yield of condensed tannins and Stiasny index for studied clones are low, showing the infeasibility of using bark for the extraction of tannins to produce adhesives, however tannins and other bioactive phenolic compounds can be used in the pharmaceutical and cosmetics sectors due to its antioxidant potential. The spectrum of tannins is the same as the one found the literature. Due to the high yield of verified sugar, (around 46,68%) sugars are potencial products, with a high yield of glucose , it is interesting for application in biorefinery.

Potencial da espectroscopia no infravermelho próximo para distinção de carvão de madeira de Eucalyptus e nativa

The objective of this study was to evaluate the potential of near infrared spectroscopy (NIRS) associated with multivariate statistics to distinguish coal produced from wood of planted and native forests. Timber forest species from the C errado (Cedrela sp., Aspidosperma sp., Jacaranda sp. and unknown species) and Eucalyptus clones from forestry companies (Vallourec and Cenibra) were carbonized in the final temperatures of 300, 500 and 700°C. In each heat treatment were carbonized 15 specimens of each vegetal material totaling 270 samples (3 treatments x 15 reps x 6 materials) produced in 18 carbonization (3 treatments x 6 materials). The acquisition of the spectra of coals in the near infrared using a spectrometer was performed. Principal Component Analysis (PCA) and Partial Least Squares Regression (PLS-R) were carried out in the spectra. NIR Spectroscopy associated with PCA was not able to differentiate charcoals produced from native and planted woods when utilizing all carbonized samples at different temperatures in the same analysis; The PCA of all charcoals was able to distinguish the samples depending on temperature in which they were carbonized. However, the separation of native and planted charcoal was possible when the samples were analyzed separately by final temperature. The prediction of native or planted classes by PLS-R presented better performance for samples carbonized at 300°C followed by those at 500°C, 700°C and for all together.

Análise energética da madeira e do carvão de híbridos entre Corymbia citriodora (Hook.) K.D. Hill & L.A.S. Johnson e Corymbia torelliana (F. Muell.) K.D. Hill & L.A.S. Johnson

This research aimed to evaluate the wood and charcoal quality of hybrids clone of the crossing C. citriodora with C. torelliana in two different locations for charcoal production. Seven with 3,75 years old clones, planted at country of Itamarandiba – MG, and six 6,42 years old clones, planted in Dionísio – MG, were studied. For wood and charcoal quality analysis, samples were collected along the stem of the trees until the commercial height. Properties study of the wood was done by chemical analysis, basic density, superior heat power, and thermogravimetric analysis. The wood samples were carbonized in laboratory conditions with heating rate of 1.67 0 C.min -1 , starting at 100 0 C until 450 0 C and keeping on this temperature for 30 minutes. It were determined the carbonizations gravimetric yield, all in dry basis. The wood quality was evaluated based on the chemical immediate analysis, relative apparent density, and gross heating value. The experiment was installed according to the completely randomized design, with five repetitions. The collected data were submitted to analysis of variance and, when the evaluated effects were significant by “F” test, was applied the Scott-Knott test at 5% probability for multiple comparisons. For correlation analysis, Pearson correlation coefficient, tested by the "t" test at 5% probability was used. Results showed variability of wood between the genetic materials evaluated in relation to place and plant crossing. The thermal analysis of the wood showed significant variation between clones and it was possible to differentiate two stages of degradation (hemicelluloses and cellulose). The majority of the clones presented satisfactory properties for the charcoal production, while, clone 3, planted in Itamarandiba, obtained the best performance due it have the higher yield and energetic efficiency, thus, achieving the best potential for charcoal production. However, clone 9, planted in Dionísio, was the less indicated for charcoal production since it presented the lowest energetic efficiency, gravimetric yield, and densities.