Synthesis of 4-arm star poly(L-Lactide) oligomers using an in situ-generated calcium-based initiator

Using an in situ-generated calcium-based initiating species derived from pentaerythritol, the bulk synthesis of well-defined 4-arm star poly(L-lactide) oligomers has been studied in detail. The substitution of the traditional initiator, stannous octoate with calcium hydride allowed the synthesis of oligomers that had both low PDIs and a comparable number of polymeric arms (3.7 – 3.9) to oligomers of similar molecular weight. Investigations into the degree of control observed during the course of the polymerization found that the insolubility of pentaerythritol in molten L-lactide resulted in an uncontrolled polymerization only when the feed mole ratio of L-lactide to pentaerythritol was 13. At feed ratios of 40 and greater, a pseudo-living polymerization was observed. As part of this study, in situ FT-Raman spectroscopy was demonstrated to be a suitable method to monitor the kinetics of the ring-opening polymerization (ROP) of lactide. The advantages of using this technique rather than FT-IR-ATR and 1H NMR for monitoring L-lactide consumption during polymerization are discussed.

Living characteristics of the free-radical ring-closing polymerization of diallyldimethylammonium chloride

In this communication we provide the most recent results on RAFT-mediated ring-closing polymerization of diallyldimethylammonium chloride (DADMAC). The polymerization was carried out in aqueous solution employing 2,2′-azobis(2-methylpropionamidine)-dihydrochloride as the free radical initiator and trithiocarbonate RAFT agent (2-{[(dodecylsulfanyl)carbonothioyl sulfanyl]}propanoic acid, DoPAT) as the controlling RAFT agent. The results show that – while the system is not as completely controlled as previously described – it is nevertheless possible to mediate the polymerization of DADMAC and impart some living characteristics onto the system. The initial study on the RAFT-mediated polymerization of DADMAC may have overestimated the degree of livingness within this reaction. However, it is possible – at low conversions – for some living characteristics to be observed, as the evolution of molecular weight with conversion is linear. In addition, polymers with a reasonably narrow polydispersity can be isolated.

Methacrylate-functionalized oligomers based on lactide, E-caprolactone and trimethylene carbonate for application in stereo-lithography

Photo-curable biodegradable macromers were prepared by ring opening polymerization of D,L-lactide (DLLA), (similar to)-caprolactone (CL) and 1,3-trimethylene carbonate (TMC) in the presence of glycerol or sorbitol as initiator and stannous octoate as catalyst, and subsequent methacrylation of the terminal hydroxyl groups. These methacrylated macromers, ranging in molecular weight from approximately 700 to 6000 g/mol, were cross-linked using ultraviolet (UV) light to form biodegradable networks. Homogeneous networks with high gel contents were prepared. One of the resins based on PTMC was used to prepare three-dimensional structures by stereo-lithography using a commercially available apparatus.

Methacrylate-functionalized oligomers based on lactide, ε- caprolactone and trimethylene carbonate for application in stereo-lithography

Photo-curable biodegradable macromers were prepared by ring opening polymerization of D,L-lactide (DLLA), ε-caprolactone (CL) and 1,3-trimethylene carbonate (TMC) in the presence of glycerol or sorbitol as initiator and stannous octoate as catalyst, and subsequent methacrylation of the terminal hydroxyl groups. These methacrylated macromers, ranging in molecular weight from approximately 700 to 6000 g/mol, were cross-linked using ultraviolet (UV) light to form biodegradable networks. Homogeneous networks with high gel contents were prepared. One of the resins based on PTMC was used to prepare three-dimensional structures by stereo-lithography using a commercially available apparatus.

Raman spectroscopy of some complex arsenate minerals—implications for soil remediation

The application of spectroscopy to the study of contaminants in soils is important. Among the many contaminants is arsenic, which is highly labile and may leach to non-contaminated areas. Minerals of arsenate may form depending upon the availability of specific cations for example calcium and iron. Such minerals include carminite, pharmacosiderite and talmessite. Each of these arsenate minerals can be identified by its characteristic Raman spectrum enabling identification.

Raman spectroscopy of synthetic CaHPO4•2H2O– and in comparison with the cave mineral brushite

The mineral brushite has been synthesised by mixing calcium ions and hydrogen phosphate anions to mimic the reactions in a Cave. The vibrational spectra of the synthesised brushite were compared with that of the natural Cave mineral. Bands attributable to the PO43- and HPO42- anions are observed. Brushite, both synthetic and natural, is characterised by an intense sharp band at 985 cm-1 with a shoulder at 1000 cm-1. Characteristic bending modes are observed in the 300 to 600 cm-1 region. The spectra of the synthesised brushite matches very well the spectrum of brushite from the Moorba Cave, Western Australia.

Poly(2-oxazoline) hydrogel monoliths via thiol-ene coupling

Copoly(2-oxazoline)s, prepared by cationic ring-opening polymerization of 2-(dec-9-enyl)-2-oxazoline with either 2-methyl-2-oxazoline or 2-ethyl-2-oxazoline, have been crosslinked with small dithiol molecules under UV-irradiation to form homogeneous networks. In-situ monitoring of the crosslinking reaction by photo-rheology revealed network formation within minutes. The degree of swelling in water was found to be tunable by the hydrophilicity of the starting macromers and the proportion of alkene side arms. Furthermore, degradable hydrogels have been prepared based on a hydrolytically cleavable dithiol crosslinker.

Poly(2-oxazoline) hydrogels for controlled fibroblast attachment

Currently there is a lack of choice when selecting synthetic materials with the cell-instructive properties demanded by modern biomaterials. The purpose of this study was to investigate the attachment of cells onto hydrogels prepared from poly(2-oxazoline)s selectively-functionalized with cell adhesion motifs. A water-soluble macromer based on the microwave-assisted cationic ring-opening polymerization of 2-methyl-2-oxazoline and 2-(dec-9-enyl)-2-oxazoline was functionalized with the peptide CRGDSG or controls using thiol-ene photochemistry followed by facile crosslinking in the presence of a dithiol crosslinker. The growth of human fibroblasts on the hydrogel surfaces was dictated by the structure and amount of incorporated peptide. Controls without any peptide showed resistance to cellular attachment. The benignity of the crosslinking conditions was demonstrated by the incorporation of fibroblasts within the hydrogels to produce three-dimensional cell-polymer constructs.

Raman spectroscopy of the molybdate minerals chillagite (tungsteinian wulfenite-I4), stolzite, scheelite, wolframite and wulfenite

Raman spectra of chillagite, wulfenite, stolzite, scheelite and wolframite were obtained at 298 and 77 K using a Raman microprobe in combination with a thermal stage. Chillagite is a solid solution of wulfenite and stolzite. The spectra of these molybdate minerals are orientation dependent. The band at 695 cm-1 is interpreted as an antisymmetric bridging mode associated with the tungstate chain. The bands at 790 and 881 cm-1 are associated with the antisymmetric and symmetric Ag modes of terminal WO2 whereas the origin of the 806 cm-1 band remains unclear. The 4(Eg) band was absent for scheelite. The bands at 353 and 401 cm-1 are assigned as either deformation modes or as r(Bg) and (Ag) modes of terminal WO2. The band at 462 cm-1 has an equivalent band in the infrared at 455 cm-1 assigned as as(Au) of the (W2O4)n chain. The band at 508 cm-1 is assigned as sym(Bg) of the (W2O4)n chain.

Raman spectroscopy of kaolinites using different excitation wavelengths

The Raman spectra of both low- and high-defect kaolinites in the hydroxyl stretching and low-wavenumber region were obtained with excitation at three visible wavelengths of 633, 514 and 442 nm and a UV wavelength of 325 nm. The UV-excited spectra were comparable to those excited by the visible wavelengths. The Raman spectra show hydroxyl stretching bands at 3621 cm-1 attributed to the inner hydroxyl, at 3692 and 3684 cm-1 attributed to the longitudinal and transverse optic modes of the inner surface hydroxyls and at 3668 and 3653 cm-1 assigned to the out-of phase vibrations of the inner surface hydroxyls. Two bands were observed in the spectral profile at 3695 cm-1 for the high-defect kaolinite at 3698 and 3691 cm-1 and were assigned to TO/LO splitting. An increase in relative intensity of the transverse optic mode is observed with decrease in laser wavelength. The intensity of the out-of-phase vibrations at 3668 and 3653 cm-1 of the inner surface hydroxyls shows a linear relationship with the longitudinal and transverse optic modes. In the low-wavenumber region excellent correlation was found between the experimentally determined and the calculated band positions.

Raman spectroscopy of the copper chloride minerals nantokite, eriochalcite and claringbullite - implications for copper corrosion

The application of Raman spectroscopy to the study of the copper chloride minerals nantokite, eriochalcite and claringbullite has enabled the vibrational modes for the CuCl, CuOH and CuOH2 to be determined. Nantokite is characterised by bands at 205 and 155 cm-1 attributed to the transverse and longitudinal optic vibrations. Nantokite also has an intense band at 463 cm-1, eriochalcite at 405 and 390 cm-1 and claringbullite at 511 cm-1. These bands are attributed to CuO stretching modes. Water librational bands at around 672 cm-1 for eriochalcite have been identified and hydroxyl deformation modes of claringbullite at 970, 906 and 815 cm-1 are observed. Spectra of the three minerals are so characteristically different that the minerals are readily identified by Raman spectroscopy. The minerals are often determined in copper corrosion products by X-ray diffraction. Raman spectroscopy offers a rapid, in-situ technique for the identification of these corrosion products.