Edge-defined, film-fed growth (EFG) technique for the preparation of alpha-Al2O3 : C crystal with highly sensitive thermoluminescence response

In this work, alpha-Al2O3:C, a highly sensitive thermoluminescence dosimetry crystal, was grown by the EFG method in which a graphite heating unit and shield acted as the carbon source during the growth process. The optical, luminescent properties and dosimetric characteristics of the crystal were investigated. The as-grown crystal shows a single glow peak at 536 K, which is associated with Cr3+ ions. After annealing in H-2 at 1673 K for 80 h, the crystal shows a single glow peak at 460 K and a blue emission band at 415 nm. The thermoluminescent response of the annealed crystal shows linear-sublinear-saturation characteristics in the dose range from 5 x 10(-6) to 100 Gy.

Anisotropic crystallographic properties, strain, and their effects on band structure of m -plane GaN on LiAlO2 (100)

The m-plane GaN films grown on LiAlO2(100) by metal-organic chemical vapor deposition exhibit anisotropic crystallographic properties. The Williamson-Hall plots point out they are due to the different tilts and lateral correlation lengths of mosaic blocks parallel and perpendicular to GaN[0001] in the growth plane. The symmetric and asymmetric reciprocal space maps reveal the strain of m-plane GaN to be biaxial in-plane compress epsilon(xx)=-0.79% and epsilon(zz)=-0.14% with an out-of-plane dilatation epsilon(yy)=0.38%. This anisotropic strain further separates the energy levels of top valence band at Gamma point. The energy splitting as 37 meV as well as in-plane polarization anisotropy for transitions are found by the polarized photoluminescence spectra at room temperature. (c) 2008 American Institute of Physics.

Growth of highly sensitive thermoluminescent crystal alpha-Al2O3 : C by the temperature gradient technique

In this work, an alpha-Al2O3:C crystal with highly sensitive thermoluminescence was directly grown by the temperature gradient technique (TGT) using Al2O3 and graphite powders as raw materials. The optical and luminescent properties and the dosimetric characteristics of the crystal were investigated. An as-grown alpha-Al2O3:C crystal shows a single glow peak at 462 K and a blue emission peak at 415 nm. The thermoluminescence (TL) response of the crystal shows a linear-sublinear-saturation characteristic. In the dose range from 5 x 10(-6) to 10Gy, the alpha-Al2O3:C crystal shows excellent linearity, and saturation was observed at about 30Gy. The sensitivity of the crystal decreases as the heating rate increases. (c) 2008 Elsevier B.V. All rights reserved.

Growth of alpha-Al2O3:C crystal with highly sensitive optically stimulated luminescence

In this work. an alpha-Al2O3:C crystal was directly grown by the temperature gradient technique (TGT) using Al2O3 and graphite powders as the raw materials. The optical, optically stimulated luminescence (OSL) properties and dosimetric characteristics of as-grown crystal were investigated. As-grown alpha-Al2O3:C crystal shows strong absorption band at 205, 230 and 256 nm. Three-dimensional thermoluminescence (TL) emission spectrum of the crystal shows a single emission peak at similar to 415 nm. The OSL decay curve can be fitted to two exponentials, the faster component and the slower component. The OSL response of the crystal shows a linear-sublinear-saturation characteristic. As-grown alpha-Al2O3:C crystal shows excellent linearity in the dose range from 5 x 10(-6) to 50 Gy. For doses higher than the saturation dose (100 Gy). the OSL sensitivity decreases as the dose increases. Crown Copyright (C) 2008 Published by Elsevier B.V. All rights reserved.