An electroanalytical application of 2-aminothiazole-modified silica gel after adsorption and separation of Hg(II) from heavy metals in aqueous solution

2-Aminothiazole covalently attached to a silica gel surface was prepared in order to obtain an adsorbent for Hg(II) ions having the following characteristics: good sorption capacity, chemical stability under conditions of use, and, especially, high selectivity. The accumulation voltammetry of mercury(II) was investigated at a carbon paste electrode chemically modified with silica gel functionalized with 2-aminothiazole (SIAMT-CPE). The repetitive cyclic voltammogram of mercury(II) solution in the potential range -0.2 to + 0.6 V versus Ag/AgCl (0.02 mol L-1 KNO3; V = 20 mV s(-1)) show two peaks one at about 0.1 V and other at 0.205 V. The anodic wave peak at 0.205 V is well defined and does not change during the cycles and it was therefore further investigated for analytical purposes using differential pulse anodic stripping voltammetry in differents supporting electrolytes. The mercury response was evaluated with respect to pH, electrode composition, preconcentration time, mercury concentration, cleaning solution, possible interferences and other variables. The precision for six determinations (n = 6) of 0.02 and 0.20 mg L-1 Hg(II) was 4.1 and 3.5% (relative standard deviation), respectively. The detection limit was estimated as 0.10 mu g L-1 mercury(II) by means of 3:1 current-to-noise ratio in connection with the optimization of the various parameters involved and using the highest-possible analyser sensitivity. (c) 2006 Elsevier Ltd. All rights reserved.

Al-based anodic oxide films structure observation using field emission gun scanning electron microscopy

In the present work, the anodic oxide films of Al, Al-Cu 4.5% and Al-Si 6.5% alloys are formed using direct and pulse current. In the case of Al-Cu and Al-Si alloys, the electrolyte used contains sulfuric acid and oxalic acid, meanwhile for Al the electrolyte contains sulfuric acid only. Al-Cu alloy was submitted to a heat treatment in order to decrease the effect of inter metallic phase theta upon the anodic film structure. Fractured samples were observed using a field emission gun scanning electron microscope JSM-6330F at (LME)/Brazilian Synchrotron Light Laboratory (LNLS), Campinas, SP, Brazil. The oxide film images enable evaluation of the pore size and form with a resolution similar to the transmission electron microscope (TEM) resolution. It is also observed that the anodizing process using pulse current produces an irregular structure of pore walls, and by direct cur-rent it is produced a rectilinear pore wall. (c) 2005 Elsevier B.V. All rights reserved.