Phase Evolution in the AuCu/Sn System by Solid-State Reactive Diffusion
Data(s) |
2014
|
---|---|
Resumo |
The interfacial reactions between several Au(Cu) alloys and pure Sn were studied experimentally at 200A degrees C. Amounts of Cu in the AuSn4 and AuSn2 phases were as low as 1 at.%. On the basis of these experimental results there is no continuous solid solution between (Au,Cu)Sn and (Cu,Au)(6)Sn-5. The copper content of (Au,Cu)Sn was determined to be approximately 7-8 at.%. Substantial amounts of Au were present in the (Cu,Au)(6)Sn-5 and (Cu,Au)(3)Sn phases. Two ternary compounds were formed, one with stoichiometry varying from (Au40.5Cu39)Sn-20.5 to (Au20.2Cu59.3)Sn-20.5 (ternary ``B''), the other with the composition Au34Cu33Sn33 (ternary ``C''). The measured phase boundary compositions of the product phases are plotted on the available Au-Cu-Sn isotherm and the phase equilibria are discussed. The complexity and average thickness of the diffusion zone decreases with increasing Cu content except for the Au(40 at.%Cu) couple. |
Formato |
application/pdf |
Identificador |
http://eprints.iisc.ernet.in/49888/1/jou_ele_mat_43-9_3357_2014.pdf Santra, Sangeeta and Islam, Sarfaraj and Ravi, Raju and Vuorinen, Vesa and Laurila, Tomi and Paul, Aloke (2014) Phase Evolution in the AuCu/Sn System by Solid-State Reactive Diffusion. In: JOURNAL OF ELECTRONIC MATERIALS, 43 (9). pp. 3357-3371. |
Relação |
http://dx.doi.org/ 10.1007/s11664-014-3241-z http://eprints.iisc.ernet.in/49888/ |
Palavras-Chave | #Materials Engineering (formerly Metallurgy) |
Tipo |
Journal Article PeerReviewed |